Microstructure and magnetoelasticity of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) alloys
文献类型：期刊论文
| 作者 | B. W. Wang ; S. C. Busbridge ; R. G. Yan ; S. Y. Cao ; W. M. Huang |
| 刊名 | Ieee Transactions on Magnetics
 |
| 出版日期 | 2004 |
| 卷号 | 40期号:4页码:2769-2771 |
| 关键词 | rare-earth iron compound melt-spun ribbon magnetostriction magnetoelastic magnetostriction |
| ISSN号 | 0018-9464 |
| 中文摘要 | The microstructure and magnetoelasticity of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) alloys have been investigated using X-ray diffraction, transmission electron microscopy, three-terminal capacitance and standard strain gauge techniques. The microstructure of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) is a mixture of (Sm,Pr)Fe-2/(Sm,Pr)(Fe,B)(2) crystalline and amorphous phases. The amount of amorphous phase with increasing Pr or B content. The microstructure of Sm0.9Pr0.1(Fe0.8B0.2)(2) is almost entirely amorphous phase. The magnetostriction of melt-spun Sm1-xPrxFe2 remains almost unchanged when x < 0.1 but decreases with increasing x when x > 0.1. The magnetostriction of Sm0.9Pr0.1(Fe1-yBy)(2) decreases with increasing y in high magnetic fields, but increases with increasing y in low fields (H < 400 kA/m) due to the existence of the amorphous phase. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35572]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | B. W. Wang,S. C. Busbridge,R. G. Yan,et al. Microstructure and magnetoelasticity of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) alloys[J]. Ieee Transactions on Magnetics,2004,40(4):2769-2771. |
| APA | B. W. Wang,S. C. Busbridge,R. G. Yan,S. Y. Cao,&W. M. Huang.(2004).Microstructure and magnetoelasticity of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) alloys.Ieee Transactions on Magnetics,40(4),2769-2771. |
| MLA | B. W. Wang,et al."Microstructure and magnetoelasticity of melt-spun Sm1-xPrxFe2 and Sm0.9Pr0.1(Fe1-yBy)(2) alloys".Ieee Transactions on Magnetics 40.4(2004):2769-2771. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。