Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys
文献类型：期刊论文
| 作者 | Q. M. Wang ; Y. N. Wu ; P. L. Ke ; H. T. Cao ; J. Gong ; C. Sun ; L. S. Wen |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2004 |
| 卷号 | 186期号:3页码:389-397 |
| 关键词 | NiCoCrAlY NiCoCrAlYSiB arc ion plating AIP hot corrosion molten sulfate protective-coatings oxidation behavior mcraly coatings alloys |
| ISSN号 | 0257-8972 |
| 中文摘要 | NiCoCrAlY(SiB) coatings were deposited on the nickel base superalloys DZ125 and DSM11 by arc ion plating (AIP). The corrosion behavior of the bare alloys and the protective coatings in molten 75 wt.% Na2SO4 + 25 wt.% K2SO4 at 900degreesC in air was tested for 90 h. The results indicated that DZ125 superalloy suffered catastrophic corrosion after 5 It exposure and a thick porous oxide scale (500-600 mum) interspersed with Ni3S2 and alloy particles formed on the alloy. For the Cr-rich DSM11 alloy, a mild corrosion attack happened, but severe internal Al-rich oxidation occurred inside the alloy. With NiCoCrAlY and NiCoCrAlYSiB coatings, the hot corrosion resistance of the systems was improved due to the formation of an alpha-Al2O3 scale. The hot corrosion resistance of the coatings with additions of Si and B can be improved by promoting the growth of a dense and continuous alpha-Al2O3 layer in the initial stage and improving the adherence of the oxide scale to the coating in the subsequent hot corrosion process. The hot corrosion degradation mechanism of the NiCoCrAlYSiB coatings and the influence of the substrate materials on the behavior of the whole system were also investigated. (C) 2004 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35588]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. M. Wang,Y. N. Wu,P. L. Ke,et al. Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys[J]. Surface & Coatings Technology,2004,186(3):389-397. |
| APA | Q. M. Wang.,Y. N. Wu.,P. L. Ke.,H. T. Cao.,J. Gong.,...&L. S. Wen.(2004).Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys.Surface & Coatings Technology,186(3),389-397. |
| MLA | Q. M. Wang,et al."Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys".Surface & Coatings Technology 186.3(2004):389-397. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。