The corrosion behavior of four commercial steels in reducing atmospheres containing HCl at 773-873 K
文献类型：期刊论文
| 作者 | K. Zhang ; Y. Niu ; M. Al-Omary ; W. T. Wu |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2004 |
| 卷号 | 62期号:5-6页码:323-340 |
| 关键词 | Cr steels HCl reducing atmosphere corrosion high-temperature corrosion fe-cr alloys hydrogen-chloride chromium-alloys gas-mixtures oxygen 800-degrees-c oxidation metals fuels |
| ISSN号 | 0030-770X |
| 中文摘要 | The corrosion of four Fe-Cr commercial steels with different tents in a simulated waste-gasification atmosphere containing 0.5 vol.% H-2, 0.5 vol.% HCl, balance CO2 has been investigated at 773 and 873 K. The same materials have also been tested in the same gas mixture free from HCl at both temperatures for comparison. The results show that the materials with low-chromium content (2.25 CrMoV and NF616) undergo accelerated corrosion in the presence of HCl, while the stainless steel SS304 suffers very little corrosion. On the contrary a steel containing 12 wt.% Cr (12 CrMoV) corrodes rather rapidly at 773 K but quite slowly at 873 K. The beneficial effect of chromium on the corrosion resistance of the steels increases with the chromium content at both temperatures. The steels tested show corrosion rates generally decreasing with time, having kinetics which are approximately parabolic at 773 K but intermediate between parabolic and linear at 873 K Only little or even no chlorine can be detected at the scale/metal interface at both temperatures for all materials corroded in HO-containing atmospheres. The corrosion mechanism can be explained by the so-called "active-oxidation, model. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35712]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. Zhang,Y. Niu,M. Al-Omary,et al. The corrosion behavior of four commercial steels in reducing atmospheres containing HCl at 773-873 K[J]. Oxidation of Metals,2004,62(5-6):323-340. |
| APA | K. Zhang,Y. Niu,M. Al-Omary,&W. T. Wu.(2004).The corrosion behavior of four commercial steels in reducing atmospheres containing HCl at 773-873 K.Oxidation of Metals,62(5-6),323-340. |
| MLA | K. Zhang,et al."The corrosion behavior of four commercial steels in reducing atmospheres containing HCl at 773-873 K".Oxidation of Metals 62.5-6(2004):323-340. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。