Cross-sectional oxide distribution of cast IN738 and its sputtered coating at 1000 degrees C
文献类型：期刊论文
| 作者 | S. J. Geng ; F. H. Wang ; S. Zhang |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2003 |
| 卷号 | 167期号:2-3页码:161-164 |
| 关键词 | IN738 alloy sputtering nanocrystalline coating oxidation oxidation behavior high-temperature selective oxidation superalloy k38g resistance |
| ISSN号 | 0257-8972 |
| 中文摘要 | A sputtered nanocrystalline coating of IN738 alloy was obtained by means of magnetron sputtering technique. The oxide distribution was presented of the cast IN738 and its coating after 50 h in air at 1000degreesC. The results indicated that the oxide scale formed on the cast alloy consisted roughly of three sections: the top-most section being Cr2O3 and TiO2 mixture, followed by internal aluminum oxide, and scattering beneath which being TiN particles. In the case of nanocrystalline coating, however, only two sections were obvious: the top Cr2O3, TiO2 and NiCr2O4 spinel mixture layer and the inner continuous Al2O3 layer. No internal oxidation and nitridation occurred. (C) 2002 Elsevier Science B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35835]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. J. Geng,F. H. Wang,S. Zhang. Cross-sectional oxide distribution of cast IN738 and its sputtered coating at 1000 degrees C[J]. Surface & Coatings Technology,2003,167(2-3):161-164. |
| APA | S. J. Geng,F. H. Wang,&S. Zhang.(2003).Cross-sectional oxide distribution of cast IN738 and its sputtered coating at 1000 degrees C.Surface & Coatings Technology,167(2-3),161-164. |
| MLA | S. J. Geng,et al."Cross-sectional oxide distribution of cast IN738 and its sputtered coating at 1000 degrees C".Surface & Coatings Technology 167.2-3(2003):161-164. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。