High temperature oxidation behavior of a sputtered pure Ni nanocrystalline coating at 700-900 degrees C
文献类型：期刊论文
| 作者 | S. J. Geng ; F. H. Wang ; S. Zhang |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2003 |
| 卷号 | 167期号:2-3页码:212-216 |
| 关键词 | pure Ni sputtering nanocrystalline coating oxidation corrosion-resistance selective oxidation k38g alloy superalloy oxygen |
| ISSN号 | 0257-8972 |
| 中文摘要 | A nanocrystalline coating of Ni was deposited on a pure Ni substrate via magnetron sputtering. The oxidation behavior of the Ni substrate and the nanocrystalline coating was studied in air at 700-900degreesC. The samples were examined by scanning tunneling microscopy, scanning electron microscopy with energy dispersive X-ray and X-ray diffraction. The mass gain in the coated sample was higher than that without the coating. The study showed that the nanocrystallization in pure Ni promoted oxidation during early stage, after that, the oxidation rates are about the same in samples with or without the nanocrystalline layer. The oxidation mechanism was also discussed. (C) 2003 Elsevier Science B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35836]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. J. Geng,F. H. Wang,S. Zhang. High temperature oxidation behavior of a sputtered pure Ni nanocrystalline coating at 700-900 degrees C[J]. Surface & Coatings Technology,2003,167(2-3):212-216. |
| APA | S. J. Geng,F. H. Wang,&S. Zhang.(2003).High temperature oxidation behavior of a sputtered pure Ni nanocrystalline coating at 700-900 degrees C.Surface & Coatings Technology,167(2-3),212-216. |
| MLA | S. J. Geng,et al."High temperature oxidation behavior of a sputtered pure Ni nanocrystalline coating at 700-900 degrees C".Surface & Coatings Technology 167.2-3(2003):212-216. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。