Electrochemical behavior of SUS316L stainless steel after surface modification

文献类型:期刊论文

作者C. H. Liang ; L. Guo ; W. Chen ; J. X. Liu
刊名Transactions of Nonferrous Metals Society of China
出版日期2003
卷号13期号:2页码:398-401
关键词coronary stent stimulated body fluid surface modification electrochemical behavior
ISSN号1003-6326
中文摘要The surface modification for SUS316L stainless steel was carried out by electroplating Rh, ion beam assisted deposition Ta2O5 and sol-gel-derived TiO2. In Tyrode's stimulated body fluid, the surface modified samples were investigated with electrochemical techniques. The results indicate that the electrochemical stability and dissolution are improved significantly after surface modification. Moreover, as to ion beam assisted deposition Ta2O5 and sol-gel-derived TiO2 film, the metal's d orbit electron holes filled up by the oxygen electrons make against the adsorption of hydrogen. Thus the cathode process, which is controlled by the hydrogen reduction, is held back. X-ray diffraction analysis of SUS316L stainless steel after surface modification reveal that each method forms the uniform and compact film on SUS316L stainless steel. These films prevent the dissolving of elements and improve passivation property of the SUS316L stainless steel.
原文出处://WOS:000182726000034
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/35910]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
C. H. Liang,L. Guo,W. Chen,et al. Electrochemical behavior of SUS316L stainless steel after surface modification[J]. Transactions of Nonferrous Metals Society of China,2003,13(2):398-401.
APA C. H. Liang,L. Guo,W. Chen,&J. X. Liu.(2003).Electrochemical behavior of SUS316L stainless steel after surface modification.Transactions of Nonferrous Metals Society of China,13(2),398-401.
MLA C. H. Liang,et al."Electrochemical behavior of SUS316L stainless steel after surface modification".Transactions of Nonferrous Metals Society of China 13.2(2003):398-401.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。