Corrosion behavior and strength degradation of Ti3SiC2 exposed to a eutectic K2CO3 and Li2CO3 mixture
文献类型：期刊论文
| 作者 | G. M. Liu ; M. S. Li ; Y. C. Zhou ; Y. M. Zhang |
| 刊名 | Journal of the European Ceramic Society
 |
| 出版日期 | 2003 |
| 卷号 | 23期号:11页码:1957-1962 |
| ISSN号 | 0955-2219 |
| 关键词 | carbonate melt corrosion fracture strength molten salts Ti3SiC2 titanium-silicon carbide hot corrosion bulk ceramics |
| 中文摘要 | The corrosion of polycrystalline Ti3SiC2 was studied in the eutectic Li2CO3 (68 at.%) and K2CO3 (32 at.%) Mixture at 650-850degreesC. Ti3SiC2 exhibited better corrosion resistance at 650 degreesC. However, the mass loss was fast when temperature was above 700 degreesC. It was demonstrated that the surface chemical reaction-controlled shrinking core model could be applied to describe the relationship between the degree of the corrosion and reaction time for the corrosion of Ti3SiC2 in the 700-850 degreesC temperature range. The corresponding apparent activation energy was 206 kJ/mol. Corrosion resulted in roughness of specimen surface. The fracture strength of the corroded samples was evaluated by a three-point bending test. The results showed that the degradation of the fracture strength was about 25% of the original values for the corroded specimens tip to 10% weight loss. The mechanism of the strength degradation was discussed based on the analysis of the microstructure and composition of the corroded sample. (C) 2003 Elsevier Science Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35918]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. M. Liu,M. S. Li,Y. C. Zhou,et al. Corrosion behavior and strength degradation of Ti3SiC2 exposed to a eutectic K2CO3 and Li2CO3 mixture[J]. Journal of the European Ceramic Society,2003,23(11):1957-1962. |
| APA | G. M. Liu,M. S. Li,Y. C. Zhou,&Y. M. Zhang.(2003).Corrosion behavior and strength degradation of Ti3SiC2 exposed to a eutectic K2CO3 and Li2CO3 mixture.Journal of the European Ceramic Society,23(11),1957-1962. |
| MLA | G. M. Liu,et al."Corrosion behavior and strength degradation of Ti3SiC2 exposed to a eutectic K2CO3 and Li2CO3 mixture".Journal of the European Ceramic Society 23.11(2003):1957-1962. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。