Morphologic investigation and growth of the alumina scale on magnetron-sputtered CoCrAlNCs with and without yttrium
文献类型：期刊论文
| 作者 | X. Peng ; F. Wang |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2003 |
| 卷号 | 45期号:10页码:2293-2306 |
| 关键词 | oxide growth oxidation CoCrAl yttrium magnetron-sputtering nanocoating fe-cr-al oxidation behavior reactive elements oxide scales alloys segregation resistance mechanism additions coatings |
| ISSN号 | 0010-938X |
| 中文摘要 | Nanostructured coatings exhibit superior oxidation resistance due to preferable formation of pure alpha-Al2O3 scale. In this work, the morphology and growth of the scale formed on magnetron-sputtered CoCrAl nanocoatings (NCs) with and without yttrium at 1000, 1100 and 1200 degreesC have been investigated in detail, by scanning electron microscopy observations of the time-dependent evolution of the scale surface and cross-sectional features. There were several observations: (1) intrinsic oxide ridges appeared on the surface scale on both NCs but their appearance was delayed on CoCrAlY, (2) CoCrAl coating tended to form a scale which was composed of multi-layered equiaxed crystals, especially at 1100 and 1200 degreesC, while the scale on CoCrAlY appeared double-layered and with inner columnar-like grains, (3) large interface cavities appeared after oxidation of CoCrAl at 1100 and 1200 degreesC but it was not be observed for oxidation of CoCrAlY. The results strongly suggest that the contribution of outward aluminum diffusion to the growth of the alpha-Al2O3 scale on both NCs is increased with an increase of time and temperature, and that it was reduced in the presence of yttrium. Additionally, compared to the scale on the normal commercial MCrAl (M = Fe, Ni, Co) alloys, the scale formed on the NCs is finer-grained and wrinkle-resistant. Based on the morphological investigation, a growth mechanism of the alumina scale on both NCs was proposed. (C) 2003 Published by Elsevier Ltd. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35997]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. Peng,F. Wang. Morphologic investigation and growth of the alumina scale on magnetron-sputtered CoCrAlNCs with and without yttrium[J]. Corrosion Science,2003,45(10):2293-2306. |
| APA | X. Peng,&F. Wang.(2003).Morphologic investigation and growth of the alumina scale on magnetron-sputtered CoCrAlNCs with and without yttrium.Corrosion Science,45(10),2293-2306. |
| MLA | X. Peng,et al."Morphologic investigation and growth of the alumina scale on magnetron-sputtered CoCrAlNCs with and without yttrium".Corrosion Science 45.10(2003):2293-2306. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。