High temperature oxidation and corrosion resistant nanocrystalline coatings
文献类型：期刊论文
| 作者 | F. Wang ; S. Geng |
| 刊名 | Surface Engineering
 |
| 出版日期 | 2003 |
| 卷号 | 19期号:1页码:32-36 |
| 关键词 | 1200 degrees c microcrystalline coatings selective oxidation aluminide coatings k38g superalloy behavior alloys platinum 900-degrees-c morphology |
| ISSN号 | 0267-0844 |
| 中文摘要 | Traditional high temperature oxidation resistant coatings are divided into three types: aluminide or modified aluminide coatings such as Cr-Al, Si-Al and Pt-Al; MCrAlY(M=Fe,Co and/or Ni) overlayer coatings and MCrAlY+Y2O3/ZrO2 thermal barrier coatings. Characteristic of these coatings is that their compositions are very different from their substrate alloys. Protection comes from the higher aluminium content in the coating to form Al2O3 at high temperature. However, these coatings may be harmful to the mechanical properties of the alloys as a result of the interdiffusion or thermal mismatch between the coating and substrate. Recently, a new kind of coating has been developed: high temperature oxidation resistant and hot corrosion resistant nanocrystalline coating, the composition of which is the same as the substrate. The only difference is that the grain size of the coating is several orders of magnitude smaller than that of the substrate. The formation of protective Al2O3 scale is not from the high aluminium. content, but from the grain boundary diffusion. The main advantages of this kind of coating are that neither interdiffusion nor thermal mismatch exist between coating and substrate. The present paper reviews the high temperature oxidation and hot corrosion resistant nanocrystalline coating with particular reference to the authors' own results. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36041]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | F. Wang,S. Geng. High temperature oxidation and corrosion resistant nanocrystalline coatings[J]. Surface Engineering,2003,19(1):32-36. |
| APA | F. Wang,&S. Geng.(2003).High temperature oxidation and corrosion resistant nanocrystalline coatings.Surface Engineering,19(1),32-36. |
| MLA | F. Wang,et al."High temperature oxidation and corrosion resistant nanocrystalline coatings".Surface Engineering 19.1(2003):32-36. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。