Structure and magnetic properties of Fe(C) and Co(C) nanocapsules prepared by chemical vapor condensation
文献类型：期刊论文
| 作者 | Z. H. Wang ; Z. D. Zhang ; C. J. Choi ; B. K. Kim |
| 刊名 | Journal of Alloys and Compounds
 |
| 出版日期 | 2003 |
| 卷号 | 361期号:1-2页码:289-293 |
| 关键词 | nanostructured materials vapour deposition crystal structure magnetic measurements transmission electron microscopy (TEM) coated fe-co(c) nanocapsules arc-discharge nanoparticles fe co methane |
| ISSN号 | 0925-8388 |
| 中文摘要 | Carbon-coated Fe and Co nanocapsules have been synthesized by a chemical vapor condensation process using carbon monoxide as carrier gas. The characterization and magnetic properties of carbon-coated Fe and Co nanocapsules are investigated and compared. The core/shell structure of the Fe(C) nanocapsules is similar to that of the Co(C) nanocapsules, consisting of an amorphous shell and a metallic core. The phases of the Co(C) nanocapsules are composed of f.c.c.-Co, h.c.p.-Co and cobalt carbides regardless of the decomposition temperature and the CO gas flow rate. The phases of the Fe(C) nanocapsules change with changing decomposition temperature and CO gas flow rate. The majority phases of the Fe(C) nanocapsules are alpha-Fe and Fe3C when the decomposition temperature is between 500 and 1000 degreesC, but for 700 degreesC only Fe3C exists alpha-Fe, gamma-Fe and Fe3C phases coexist after preparation at 1100 degreesC. The saturation magnetization of the Co(C) nanocapsules increases with increasing decomposition temperature, while that of the Fe(C) nanocapsules is less dependent on the phases formed. The cobalt nanocapsules reach 90% of the value of the saturation magnetization of bulk cobalt, while the iron nanocapsules obtained at 400 and 1100 degreesC reach 75 and 33 % of the saturation magnetization of bulk iron. The carbon-coated Fe and Co nanocapsules are shown to be ferromagnetic with a ratio of the remnant magnetization to saturation magnetization M-r/M-s of 0.3-0.4. (C) 2003 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36073]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. H. Wang,Z. D. Zhang,C. J. Choi,et al. Structure and magnetic properties of Fe(C) and Co(C) nanocapsules prepared by chemical vapor condensation[J]. Journal of Alloys and Compounds,2003,361(1-2):289-293. |
| APA | Z. H. Wang,Z. D. Zhang,C. J. Choi,&B. K. Kim.(2003).Structure and magnetic properties of Fe(C) and Co(C) nanocapsules prepared by chemical vapor condensation.Journal of Alloys and Compounds,361(1-2),289-293. |
| MLA | Z. H. Wang,et al."Structure and magnetic properties of Fe(C) and Co(C) nanocapsules prepared by chemical vapor condensation".Journal of Alloys and Compounds 361.1-2(2003):289-293. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。