Rheocast structure in a hypoeutectic high chromium white iron
文献类型：期刊论文
| 作者 | Z. Yang ; H. F. Zhang ; A. M. Wang ; B. Z. Ding ; Z. Q. Hu |
| 刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
 |
| 出版日期 | 2003 |
| 卷号 | 343期号:1-2页码:251-256 |
| 关键词 | high chromium white iron rheocast structure subgrain boundary semisolid state alloy solidification behavior flow |
| ISSN号 | 0921-5093 |
| 中文摘要 | The rheocast structure in a hypoeutectic high chromium white iron was studied. By analyzing the microstructure of the special subgrain boundaries, it was found that the solute enriched special subgrain boundaries, usually thought to be the boundaries of agglomerated separated grains, were in fact evolved from bent thin roots of dendrite arms. Further examination of the relationship between cooling rate and grain size revealed that a dendrite arm with a thin root could be bent or sheared off. At the cooling rate that favors the formation of thin rooted long dendrite arms, a fine rheocast structure can be gained. (C) 2002 Elsevier Science B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36125]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. Yang,H. F. Zhang,A. M. Wang,et al. Rheocast structure in a hypoeutectic high chromium white iron[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2003,343(1-2):251-256. |
| APA | Z. Yang,H. F. Zhang,A. M. Wang,B. Z. Ding,&Z. Q. Hu.(2003).Rheocast structure in a hypoeutectic high chromium white iron.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,343(1-2),251-256. |
| MLA | Z. Yang,et al."Rheocast structure in a hypoeutectic high chromium white iron".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 343.1-2(2003):251-256. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。