Thermal cycling behaviors of thermal barrier coatings on intermetallic Ni3Al based superalloy

文献类型:期刊论文

作者D. B. Zhang ; S. K. Gong ; H. B. Xu ; H. T. Zhang ; Y. F. Han
刊名Surface & Coatings Technology
出版日期2003
卷号168期号:1页码:78-83
关键词thermal barrier coatings electron beam physical vapor deposition Ni3Al based alloy IC6 vapor-deposition si
ISSN号0257-8972
中文摘要Ni3Al based alloy IC6, a high performance cast alloy with approximately 14 wt.% Mo addition, has been developed for turbine blades and vanes of advanced aero-engines and other high temperature structural components. However, because of the high Mo content, during high temperature use, Mo will diffuse into the protective coating layer, which will affect the thermal cycling performance directly. In order to block the diffusion and improve the thermal cycling behavior of thermal barrier coatings (TBCs), a Si chemical gradient MCrAlY-Si bond coat was prepared by changing the Si content from 0.35 wt.% at the interface of substrate and bond coat to almost 0 near to the surface of the bond coat. For comparison, conventional two-layered structural TBCs with MCrAlY as bond coat were also prepared. The fabricated coatings were evaluated for the microstructures and the composition distribution properties, such as thermal stability and resistance to oxidation. For the bond coat without Si addition, Mo, content near the surface was higher than 7 wt.% after isothermal oxidation at 1373 K for 60 h and 12.5 wt.% after thermal cycling tested at 1373 K for 300 It (600 cycles). However, in the Si chemical gradient bond coat, only 0.4 wt.% Mo was detectable after isothermal oxidation at 1373 K for 100 h and approximately 0.66 wt.% after thermal cycling tested at 1373 K for 340 h (680 cycles). (C) 2002 Elsevier Science B.V. All rights reserved.
原文出处://WOS:000182105100011
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/36152]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
D. B. Zhang,S. K. Gong,H. B. Xu,et al. Thermal cycling behaviors of thermal barrier coatings on intermetallic Ni3Al based superalloy[J]. Surface & Coatings Technology,2003,168(1):78-83.
APA D. B. Zhang,S. K. Gong,H. B. Xu,H. T. Zhang,&Y. F. Han.(2003).Thermal cycling behaviors of thermal barrier coatings on intermetallic Ni3Al based superalloy.Surface & Coatings Technology,168(1),78-83.
MLA D. B. Zhang,et al."Thermal cycling behaviors of thermal barrier coatings on intermetallic Ni3Al based superalloy".Surface & Coatings Technology 168.1(2003):78-83.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。