Hot-corrosion resistance of a sputtered K38G nanocrystalline coating in molten sulfate at 900 degrees C
文献类型：期刊论文
| 作者 | S. Geng ; F. Wang ; S. Zhu ; W. Wu |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2002 |
| 卷号 | 57期号:5-6页码:549-557 |
| 关键词 | K38G alloy sputtering coating molten sulfate corrosion superalloy oxidation |
| ISSN号 | 0030-770X |
| 中文摘要 | The hot-corrosion behavior of a nanocrystalline coating of K38G alloy, prepared by magnetron sputtering and cast K38G in molten 75 wt.% Na2SO4+25 wt.% K2SO4 at 900degreesC was studied. The coating eliminated internal sulfidation during the early stage of corrosion as a result of the formation of a continuous and compact Al2O3 scale. The nanocrystallization of K38G alloy prolonged the incubation of breakaway corrosion and improved the corrosion resistance of K38G. The relevant corrosion mechanism is discussed. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36271]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. Geng,F. Wang,S. Zhu,et al. Hot-corrosion resistance of a sputtered K38G nanocrystalline coating in molten sulfate at 900 degrees C[J]. Oxidation of Metals,2002,57(5-6):549-557. |
| APA | S. Geng,F. Wang,S. Zhu,&W. Wu.(2002).Hot-corrosion resistance of a sputtered K38G nanocrystalline coating in molten sulfate at 900 degrees C.Oxidation of Metals,57(5-6),549-557. |
| MLA | S. Geng,et al."Hot-corrosion resistance of a sputtered K38G nanocrystalline coating in molten sulfate at 900 degrees C".Oxidation of Metals 57.5-6(2002):549-557. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。