Oxidation and degradation of EB-PVD thermal-barrier coatings
文献类型：期刊论文
| 作者 | M. H. Li ; Z. Y. Zhang ; X. F. Sun ; H. R. Guan ; W. Y. Hu ; Z. Q. Hu |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2002 |
| 卷号 | 58期号:5-6页码:499-512 |
| 关键词 | magnetron sputtering electron-beam physical vapor deposition thermal barrier coating oxidation degradation |
| ISSN号 | 0030-770X |
| 中文摘要 | Thermal-barrier coatings (TBCs) consist of a magnetron-sputtered Ni-30Cr-12Al-0.3 Y (wt.%) bond coat to protect the substrate superalloy from oxidation/hot corrosion and an electron-beam physical-vapor deposited (EB-PVD) 7 wt.% yttria partially stabilized zirconia (YPSZ) top coat. The thermal cyclic life of the TBC system was assessed by furnace cycling at 1050degreesC. The oxidation kinetics were evaluated by thermogravimetric analysis (TGA) at 900, 1000, and 1100degreesC for up to 100 hr. The results showed that the weight gain of the specimens at 1100degreesC was the smallest in the initial 20 hr, and the oxide scale formed on the sputtered Ni-Cr-Al-Y bond coat is only Al2O3 at the early stage of oxidation. With aluminum depletion in the bond coat, NiO, Ni(Cr,Al)(2)O-4, and other spinel formed near the bond coat. During thermal cycling, microcracks were initiated preferentially in the YPSZ top coat along columnar grain boundaries and then extended through and along the top coat. The growth stress of TGO added to the thermal stress imposed by cycling, lead to the separation at the bond coat-TGO interface. The ceramic top coat spalled with the oxide scale still adhering to the YPSZ after specimens had been cycled at 1050degreesC for 300 cycles. The failure mode of the EB-PVD ZrO2-7 wt.% Y2O3 sputtered Ni-Cr-Al-Y thermal-barrier coating was spallation at the bond coat-TGO interface. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36312]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | M. H. Li,Z. Y. Zhang,X. F. Sun,et al. Oxidation and degradation of EB-PVD thermal-barrier coatings[J]. Oxidation of Metals,2002,58(5-6):499-512. |
| APA | M. H. Li,Z. Y. Zhang,X. F. Sun,H. R. Guan,W. Y. Hu,&Z. Q. Hu.(2002).Oxidation and degradation of EB-PVD thermal-barrier coatings.Oxidation of Metals,58(5-6),499-512. |
| MLA | M. H. Li,et al."Oxidation and degradation of EB-PVD thermal-barrier coatings".Oxidation of Metals 58.5-6(2002):499-512. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。