Influence of columnar microstructure of a sputtered NiAl coating on its oxidation behavior at 1000 degrees C
文献类型：期刊论文
| 作者 | S. L. Yang ; F. H. Wang ; Z. M. Sun ; S. L. Zhu |
| 刊名 | Intermetallics
 |
| 出版日期 | 2002 |
| 卷号 | 10期号:5页码:467-471 |
| 关键词 | nickel aluminides coatings grain boundary based on NiAl oxidation intermetallic and structure otherwise adhesion scales |
| ISSN号 | 0966-9795 |
| 中文摘要 | The influence of columnar microstructure of a sputtered nanocrystalline NiAl coating on its oxidation behavior at 1000 degreesC in air was investigated. Results showed that the existence of columnar boundaries significantly affected its initial oxidation kinetics. However, no such obvious effect on the scale thickness was observed after long term oxidation. (C) 2002 Elsevier Science Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36493]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. L. Yang,F. H. Wang,Z. M. Sun,et al. Influence of columnar microstructure of a sputtered NiAl coating on its oxidation behavior at 1000 degrees C[J]. Intermetallics,2002,10(5):467-471. |
| APA | S. L. Yang,F. H. Wang,Z. M. Sun,&S. L. Zhu.(2002).Influence of columnar microstructure of a sputtered NiAl coating on its oxidation behavior at 1000 degrees C.Intermetallics,10(5),467-471. |
| MLA | S. L. Yang,et al."Influence of columnar microstructure of a sputtered NiAl coating on its oxidation behavior at 1000 degrees C".Intermetallics 10.5(2002):467-471. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。