Effect of grain boundary orientation and cyclic load on creep and fracture behaviour in directionally solidified nickel base superalloy

文献类型:期刊论文

作者C. Yuan ; J. T. Guo ; H. C. Yang
刊名Materials Science and Technology
出版日期2002
卷号18期号:1页码:73-80
关键词alloy fatigue mechanism in738lc stress
ISSN号0267-0836
中文摘要The effects of grain boundary orientation and cyclic load on the creep and fracture behaviour of directionally solidified superalloy DZ17G have been investigated. The results show that grain boundary orientation has no effect on the creep deformation mechanism, but has a marked effect on the fracture mechanism. The creep fracture mechanism changes from a transgranular mode in longitudinal specimens to intergranular failure in transverse and inclined (45degrees to applied stress axis) specimens. Compared with constant load, cyclic load remarkably reduces creep life with the increment of cyclic frequency, but has no effect on the creep ductility. After careful examination of the transient response following the load changes, it is suggested that an intrinsic softening occurred during unloading, which accelerates the creep deformation rate on subsequent reloading, and the accumulation of this softening effect finally results in cyclic creep acceleration. The contribution of anelasticity has also been discussed.
原文出处://WOS:000174022500011
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/36516]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
C. Yuan,J. T. Guo,H. C. Yang. Effect of grain boundary orientation and cyclic load on creep and fracture behaviour in directionally solidified nickel base superalloy[J]. Materials Science and Technology,2002,18(1):73-80.
APA C. Yuan,J. T. Guo,&H. C. Yang.(2002).Effect of grain boundary orientation and cyclic load on creep and fracture behaviour in directionally solidified nickel base superalloy.Materials Science and Technology,18(1),73-80.
MLA C. Yuan,et al."Effect of grain boundary orientation and cyclic load on creep and fracture behaviour in directionally solidified nickel base superalloy".Materials Science and Technology 18.1(2002):73-80.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。