Oxidation of two ternary Cu-Ni-20 wt.% Cr alloys at 700-800 degrees C in 1 atm O-2
文献类型：期刊论文
| 作者 | Z. Q. Cao ; Y. Niu ; F. Gesmundo |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2001 |
| 卷号 | 56期号:3-4页码:287-297 |
| 关键词 | copper nickel chromium alloys oxidation 2-phase binary-alloys high-temperature oxidation most-reactive component possible scaling modes high oxidant pressures fe-cu alloys air oxidation internal oxidation stable oxide corrosion |
| ISSN号 | 0030-770X |
| 中文摘要 | Two ternary Cu-Ni-Cr alloys containing approximately 20 wt.% chromium, but with a different Cu and Ni content, have been oxidized in 1 atm of pure oxygen at 700-800 degrees C The alloy containing about 60 wt.% nickel (Cu-60Ni-20Cr) was composed of a single solid-solution phase and formed external scales of chromium ocide with an outermost layer containing a mixture of copper and nickel oxides. The alloy comprised of about 40 wt.%nickel (Cu-40Ni-2OCr) contained a mixture of two metal phases and formed complex external scales, containing copper oxide and a nickel-chromium spinel plus a region where islands of the metallic phase richer in chromium surrounded by a thin chromia layer were mixed with oxidized islands rich in copper and nickel, producing a situation out of equilibrium. With time, a very irregular and thin but essentially continuous layer of chromia formed at the base of the mixed internal region for this alloy, producing a gradual decrease of the corrosion rate down to very low values. The oxidation behavior of the two alloys is interpreted in terms of their different microstructure. In particular, the fast initial oxidation of Cu-40Ni-20Cr, associated with the formation of large amounts of copper oxides, is attributed to restrictions in chromium diffusion in the alloy due to the simultaneous presence of two metal phases. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36602]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. Q. Cao,Y. Niu,F. Gesmundo. Oxidation of two ternary Cu-Ni-20 wt.% Cr alloys at 700-800 degrees C in 1 atm O-2[J]. Oxidation of Metals,2001,56(3-4):287-297. |
| APA | Z. Q. Cao,Y. Niu,&F. Gesmundo.(2001).Oxidation of two ternary Cu-Ni-20 wt.% Cr alloys at 700-800 degrees C in 1 atm O-2.Oxidation of Metals,56(3-4),287-297. |
| MLA | Z. Q. Cao,et al."Oxidation of two ternary Cu-Ni-20 wt.% Cr alloys at 700-800 degrees C in 1 atm O-2".Oxidation of Metals 56.3-4(2001):287-297. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。