The corrosion resistance and wear resistance of thick TiN coatings deposited by arc ion plating
文献类型：期刊论文
| 作者 | F. Q. Lang ; Z. M. Yu |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2001 |
| 卷号 | 145期号:1-3页码:80-87 |
| 关键词 | thick TiN coating corrosion resistance wear resistance arc ion plating titanium behavior pvd ti(y)n films |
| ISSN号 | 0257-8972 |
| 中文摘要 | Thick TiN coatings were successfully deposited onto A3 mild steel by the arc ion plating process. The influence of the coating thickness on phase constitution of the coating and growth orientation of the crystallites was investigated using X-ray diffraction analysis. The results show that the lattice constant of the TiN coating decreased with the increase of the coating thickness from 6 to 12 mum. The wear resistance of thick TiN coatings was also studied, and results show that the arc ion plated thick TiN coatings exhibits excellent wear resistance and good adhesion to substrate. Investigation on the corrosion resistance of thick TiN coatings was performed in 450 ml of 1 N H2SO4 corrosion media by means of an electrochemical potentiodynamic polarization. The AIP TiN coatings with thickness of 12 and 18 mum show excellent corrosion resistance, and no clear corrosion pit was found on the surface of the coatings. (C) 2001 Elsevier Science B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36691]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | F. Q. Lang,Z. M. Yu. The corrosion resistance and wear resistance of thick TiN coatings deposited by arc ion plating[J]. Surface & Coatings Technology,2001,145(1-3):80-87. |
| APA | F. Q. Lang,&Z. M. Yu.(2001).The corrosion resistance and wear resistance of thick TiN coatings deposited by arc ion plating.Surface & Coatings Technology,145(1-3),80-87. |
| MLA | F. Q. Lang,et al."The corrosion resistance and wear resistance of thick TiN coatings deposited by arc ion plating".Surface & Coatings Technology 145.1-3(2001):80-87. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。