Relationship between tensile strength and preparation conditions for nickel foam
文献类型：期刊论文
| 作者 | P. S. Liu ; K. M. Liang ; S. W. Tu ; S. R. Gu ; Q. Yu ; T. F. Li ; C. Fu |
| 刊名 | Materials Science and Technology
 |
| 出版日期 | 2001 |
| 卷号 | 17期号:9页码:1069-1072 |
| ISSN号 | 0267-0836 |
| 关键词 | high-porosity metals |
| 中文摘要 | The relationship between preparation conditions and tensile strength has been investigated for a nickel foam produced by electrodeposition on an organic foam. After sintering in a NH3 decomposition atmosphere at 980 degreesC for 40 min, the results show that the tensile strength is hardly influenced by burning in air at 600 degreesC for 4 min beforehand, or by lowering the sintering temperature to 850 degreesC. During conductive treatment of the organic matrix it was found that coating with graphite base conductive colloid or chemically plating with Ni - P alloy (similar to 5 wt-%P) brought the same tensile strength for the eventual product. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36719]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | P. S. Liu,K. M. Liang,S. W. Tu,et al. Relationship between tensile strength and preparation conditions for nickel foam[J]. Materials Science and Technology,2001,17(9):1069-1072. |
| APA | P. S. Liu.,K. M. Liang.,S. W. Tu.,S. R. Gu.,Q. Yu.,...&C. Fu.(2001).Relationship between tensile strength and preparation conditions for nickel foam.Materials Science and Technology,17(9),1069-1072. |
| MLA | P. S. Liu,et al."Relationship between tensile strength and preparation conditions for nickel foam".Materials Science and Technology 17.9(2001):1069-1072. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。