Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air
文献类型:期刊论文
作者 | S. L. Yang ; F. H. Wang ; W. T. Wu |
刊名 | Intermetallics |
出版日期 | 2001 |
卷号 | 9期号:8页码:741-744 |
ISSN号 | 0966-9795 |
关键词 | nickel aluminides based on NiAl scale adhesion al2o3 scales oxide scale segregation alpha-al2o3 morphology mechanism growth |
中文摘要 | The cyclic oxidation behavior of a magnetron sputtered NiAl microcrystalline coating was investigated at 1000 degreesC in air by TGA, and SEM in comparison with cast NiAl and NiAlY alloys. Results indicate that, for the cast NiAl alloy, mass loss is observed at about 40 cycles, implying the serious spallation occurred, while no spallation is detected for NiAlY alloy and NiAl coating for the whole test period. It is evident that. the scale adhesion is improved by the microcrystallization and the addition of Y. (C) 2001 Elsevier Science Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
源URL | [http://ir.imr.ac.cn/handle/321006/36867] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | S. L. Yang,F. H. Wang,W. T. Wu. Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air[J]. Intermetallics,2001,9(8):741-744. |
APA | S. L. Yang,F. H. Wang,&W. T. Wu.(2001).Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air.Intermetallics,9(8),741-744. |
MLA | S. L. Yang,et al."Effect of microcrystallization on the cyclic oxidation behavior of beta-NiAl intermetallics at 1000 degrees C in air".Intermetallics 9.8(2001):741-744. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。