Structure and magnetic properties of boron-oxide-coated Fe(B) nanocapsules prepared by arc discharge in diborane
文献类型:期刊论文
作者 | Z. D. Zhang ; J. L. Yu ; J. G. Zheng ; I. Skorvanek ; J. Kovac ; X. L. Dong ; Z. J. Li ; S. R. Jin ; H. C. Yang ; Z. J. Guo ; W. Liu ; X. G. Zhuo |
刊名 | Physical Review B |
出版日期 | 2001 |
卷号 | 64期号:2 |
ISSN号 | 0163-1829 |
关键词 | fe-co(c) nanocapsules exchange-anisotropy carbon nanotubes particles fe alloys |
中文摘要 | The structure and magnetic properties of boron-oxide-encapsulated magnetic nanocapsules fabricated by arc discharge in diborane (B2H6) atmosphere have been investigated. The structure of boron-oxide-coated Fe(B) nanocapsules is different from that of carbon-coated nanocapsules. In contrast to carbon-coated nanocapsules consisting of a crystalline shell of graphite and a core of alpha -Fe and/or Fe3C, boron-oxide-coated Fe nanocapsules show an amorphous surface layer and a core of alpha -Fe [and alpha -Fe(B) solid solution], gamma -Fe, FeB. and/or Fe3B phases. The loop shift in the hysteresis loop indicates the existence of the exchange bias between ferromagnetic and antiferromagnetic components at room temperature. The Fe3O4 phase contributes to the exchange bias as antiferromagnetic components. A very wide energy barrier distribution exists in the Fe(B) nanocapsules. |
原文出处 | |
公开日期 | 2012-04-14 |
源URL | [http://ir.imr.ac.cn/handle/321006/36922] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Z. D. Zhang,J. L. Yu,J. G. Zheng,et al. Structure and magnetic properties of boron-oxide-coated Fe(B) nanocapsules prepared by arc discharge in diborane[J]. Physical Review B,2001,64(2). |
APA | Z. D. Zhang.,J. L. Yu.,J. G. Zheng.,I. Skorvanek.,J. Kovac.,...&X. G. Zhuo.(2001).Structure and magnetic properties of boron-oxide-coated Fe(B) nanocapsules prepared by arc discharge in diborane.Physical Review B,64(2). |
MLA | Z. D. Zhang,et al."Structure and magnetic properties of boron-oxide-coated Fe(B) nanocapsules prepared by arc discharge in diborane".Physical Review B 64.2(2001). |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。