An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049
文献类型：期刊论文
| 作者 | L. J. Chen ; Z. G. Wang ; G. Yao ; J. F. Tian |
| 刊名 | Fatigue & Fracture of Engineering Materials & Structures
 |
| 出版日期 | 2000 |
| 卷号 | 23期号:6页码:509-519 |
| 关键词 | creep-fatigue interaction life prediction nickel base superalloy low-cycle fatigue temperature 316-stainless-steel behavior growth time |
| ISSN号 | 8756-758X |
| 中文摘要 | High-temperature low-cycle fatigue tests with and without a 10-s strain hold period in a cycle were performed on a nickel base superalloy GH4049 under a fully reversed axial total strain control mode. Three creep-fatigue life prediction methods are chosen to analyse the experimental data. These methods are the linear damage summation method (LDS), the strain range partitioning method (SRP) and the strain energy partitioning method (SEP). Their ability to predict creep-fatigue lives of GH4049 at 700, 800 and 850 degrees C has been evaluated. It is found that the SEP method shows an advantage over the SRP method for all the tests under consideration. At 850 degrees C, the LDS and SEP methods give a more satisfactory prediction for creep-fatigue lives. At the temperatures of 700 and 800 degrees C, the SRP and SEP methods can correlate the life data better than the LDS method. In addition, the differences in predictive ability of these methods have also been analysed. The scanning electron microscopy (SEM) examination of fracture surfaces reveals that under creep-fatigue test conditions crack initiation mode is transgranular, while crack propagation mode is either intergranular plus transgranular or entirely intergranular, dependent on test temperature. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/36991]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. J. Chen,Z. G. Wang,G. Yao,et al. An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049[J]. Fatigue & Fracture of Engineering Materials & Structures,2000,23(6):509-519. |
| APA | L. J. Chen,Z. G. Wang,G. Yao,&J. F. Tian.(2000).An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049.Fatigue & Fracture of Engineering Materials & Structures,23(6),509-519. |
| MLA | L. J. Chen,et al."An assessment of three creep-fatigue life prediction methods for nickel-based superalloy GH4049".Fatigue & Fracture of Engineering Materials & Structures 23.6(2000):509-519. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。