Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air
文献类型：期刊论文
| 作者 | P. S. Liu ; K. M. Liang ; S. R. Gu |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2000 |
| 卷号 | 54期号:3-4页码:277-283 |
| 关键词 | aluminide coating Co-base superalloy high-temperature oxidation corrosion nodule |
| ISSN号 | 0030-770X |
| 中文摘要 | A surface-morphology change has been observed for an aluminide coating on the Go-base superalloy DZ40M during oxidation at 1100 degrees C in air. The oxide formed on the coating remained an even greyish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37102]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | P. S. Liu,K. M. Liang,S. R. Gu. Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air[J]. Oxidation of Metals,2000,54(3-4):277-283. |
| APA | P. S. Liu,K. M. Liang,&S. R. Gu.(2000).Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air.Oxidation of Metals,54(3-4),277-283. |
| MLA | P. S. Liu,et al."Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air".Oxidation of Metals 54.3-4(2000):277-283. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。