Erosion-corrosion resistant alloy development for aggressive slurry flows
文献类型：期刊论文
| 作者 | Y. G. Zheng ; Z. M. Yao ; W. Ke |
| 刊名 | Materials Letters
 |
| 出版日期 | 2000 |
| 卷号 | 46期号:6页码:362-368 |
| 关键词 | erosion-corrosion synergism material development acidic slurry sigma phase Cr-Ni-Mo steel cast-iron behavior wear steel |
| ISSN号 | 0167-577X |
| 中文摘要 | Erosion-corrosion (E-C) experiments of 316L and two sigma phase reinforced Cr-Ni-Mo steels, S1 and S2, were conducted in 10 wt% H2SO4 + 15 wt.% corundum sand to quantify the contributions of erosion, corrosion and their synergistic components to the total wear weight loss. The results showed that under severe E-C conditions, though increasing corrosion resistance was beneficial to decreasing synergistic weight loss rate, increasing erosion resistance by large amounts of sigma phase was more efficient to reduce the total weight loss rate of the steer. Therefore, the optimization of the balance between erosion and corrosion resistance to achieve the least synergistic effects between erosion and corrosion is a good way to develop the materials for slurry E-C resistance. (C) 2000 Elsevier Science B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37289]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. G. Zheng,Z. M. Yao,W. Ke. Erosion-corrosion resistant alloy development for aggressive slurry flows[J]. Materials Letters,2000,46(6):362-368. |
| APA | Y. G. Zheng,Z. M. Yao,&W. Ke.(2000).Erosion-corrosion resistant alloy development for aggressive slurry flows.Materials Letters,46(6),362-368. |
| MLA | Y. G. Zheng,et al."Erosion-corrosion resistant alloy development for aggressive slurry flows".Materials Letters 46.6(2000):362-368. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。