Structural transformations of Bi2CuO4 induced by mechanical deformation
文献类型：期刊论文
| 作者 | X. L. Chen ; J. K. Liang ; Y. Liu ; Y. C. Lan ; Y. L. Zhang ; Y. Ma ; G. C. Che ; G. D. Liu ; X. Y. Xing ; X. Y. Qiao |
| 刊名 | Journal of Applied Physics
 |
| 出版日期 | 1999 |
| 卷号 | 85期号:6页码:3155-3158 |
| 关键词 | superconducting system phases order |
| ISSN号 | 0021-8979 |
| 中文摘要 | Structural transformation of alpha-Bi2CuO4 (a = 8.4996 Angstrom, c = 5.8172 Angstrom, space group P4/ncc) during ball milling was investigated by powder x-ray diffraction and thermal analysis. It is shown that alpha-Bi2CuO4 first transforms into an amorphous phase; and then transforms into a new phase (designated by beta-Bi2CuO4) with milling time. The new phase appears to be isostructural to (La,Sr)(2)CuO4 and has a tetragonal cell with cell parameters a = 3.869 and c = 13.83 Angstrom. It is a metastable phase which can transform back into alpha-Bi2CuO4 at 650 degrees C. No superconductivity was observed above 5 K for both as-milled samples and oxygen-annealed beta-Bi2CuO4. (C) 1999 American Institute of Physics. [S0021-8979(99)02606-7]. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37329]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. L. Chen,J. K. Liang,Y. Liu,et al. Structural transformations of Bi2CuO4 induced by mechanical deformation[J]. Journal of Applied Physics,1999,85(6):3155-3158. |
| APA | X. L. Chen.,J. K. Liang.,Y. Liu.,Y. C. Lan.,Y. L. Zhang.,...&X. Y. Qiao.(1999).Structural transformations of Bi2CuO4 induced by mechanical deformation.Journal of Applied Physics,85(6),3155-3158. |
| MLA | X. L. Chen,et al."Structural transformations of Bi2CuO4 induced by mechanical deformation".Journal of Applied Physics 85.6(1999):3155-3158. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。