Deformation-induced microstructural changes in Fe40Ni40P14B6 metallic glass
文献类型：期刊论文
| 作者 | G. J. Fan ; M. X. Quan ; Z. Q. Hu ; W. Loser ; J. Eckert |
| 刊名 | Journal of Materials Research
 |
| 出版日期 | 1999 |
| 卷号 | 14期号:9页码:3765-3774 |
| 关键词 | induced nanocrystal formation amorphous-alloys fe80b20 alloy shear bands crystallization transformation state |
| ISSN号 | 0884-2914 |
| 中文摘要 | The effect of mechanical deformation via high-energy ball milling an the structure of the Fe40Ni40P14B6 metallic glass was studied by means of x-ray diffactometry, transmission electron microscopy (TEM), and differential scanning calorimetry (DSC). After 5 h of milling, TEM observations indicated that some nanocrystallites with a diameter of about 6 nm precipitated from surface layers of the amorphous ribbons, whereas the bulk remained amorphous. When milling time was increased to 11 h, bulk crystallization occurred. The amorphous Fe40Ni40P14B6 alloy crystallized into a mixture of gamma-(Fe,Ni) and (Fe,Ni)(3)(P,B). To understand the microstructural changes occurring in the amorphous ribbons before the onset of bulk crystallization, the isothermal crystallization behavior of as-deformed amorphous ribbons was studied. Compared with as-quenched amorphous ribbons, the local value of the Avrami exponent, derived from isothermal DSC data, increased from 3.5 to 4.1 for bulk crystallization. The thermal crystallization mechanism of deformed amorphous Fe40Ni40P14B6 ribbons changed from an eutectic-type reaction with simultaneous precipitation of gamma-(Fe,Ni) and (Fe,Ni)(3)(P,B) from the amorphous matrix to a primary-type reaction with precipitation of alpha-Fe(P,B) preceding the formation of gamma-(Fe,Ni) and (Fe,Ni)(3)(P,B). Our results suggest that several hours of mechanical milling cause surface crystallization and some atomic rearrangements in the amorphous alloy. The latter effect may be responsible for the observed primary-type reaction for crystallization of the deformed amorphous alloy. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37352]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. J. Fan,M. X. Quan,Z. Q. Hu,et al. Deformation-induced microstructural changes in Fe40Ni40P14B6 metallic glass[J]. Journal of Materials Research,1999,14(9):3765-3774. |
| APA | G. J. Fan,M. X. Quan,Z. Q. Hu,W. Loser,&J. Eckert.(1999).Deformation-induced microstructural changes in Fe40Ni40P14B6 metallic glass.Journal of Materials Research,14(9),3765-3774. |
| MLA | G. J. Fan,et al."Deformation-induced microstructural changes in Fe40Ni40P14B6 metallic glass".Journal of Materials Research 14.9(1999):3765-3774. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。