Amorphous forming ability in the ternary Cu-Sn-P system by mechanical alloying

文献类型:期刊论文

作者B. W. Zhang ; H. W. Xie ; S. Z. Liao
刊名Journal of Materials Processing Technology
出版日期1999
卷号90页码:378-384
关键词amorphous forming ability Cu-Sn-P alloy system mechanical alloying transition-metal alloys composition range glass-formation amorphization
ISSN号0924-0136
中文摘要Highly pure (99.9%) copper, tin and phosphorus powders of 250 mesh were thoroughly mixed to obtain the required ternary Cu86-xSnxP14 (x=2-15) alloy compositions. These mixtures were milled in a planetary ball mill. The powder samples at different intervals of milling were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). It has been found that a powder mixture of Cu84Sn2P14 amorphized after 28 h of mechanical alloying, but still some crystalline phase could be seen. When the period of milling was greater than 28 h, the intensity of thr crystalline Bragg reflexes increased with further milling. The period of complete amorphization for Cu86-xSnxP14, X=4, 5, 8 and 10 an 28, 20, 12 and 32 h, respectively. However, no typical amorphous phase was detected for the Cu71Sn15P14 mixture powders. The results show that the amorphization tendency increases first then decreases with increase of tin content, but no amorphous phase forms after the content of tin is greater than 15 wt%. The glass forming composition range in this alloy system is 4-10 wt% Sn. The amorphous forming ability for the ternary system is explained by the formation theory of amorphous alloys by one of the present authors. The formation enthalpies of the system are also calculated using Miedema's model, in order to explain the glass forming composition range. (C) 1999 Elsevier Science S.A. All rights reserved.
原文出处://WOS:000080762300063
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/37569]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
B. W. Zhang,H. W. Xie,S. Z. Liao. Amorphous forming ability in the ternary Cu-Sn-P system by mechanical alloying[J]. Journal of Materials Processing Technology,1999,90:378-384.
APA B. W. Zhang,H. W. Xie,&S. Z. Liao.(1999).Amorphous forming ability in the ternary Cu-Sn-P system by mechanical alloying.Journal of Materials Processing Technology,90,378-384.
MLA B. W. Zhang,et al."Amorphous forming ability in the ternary Cu-Sn-P system by mechanical alloying".Journal of Materials Processing Technology 90(1999):378-384.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。