Cu/Ti3SiC2 composite: a new electrofriction material
文献类型：期刊论文
| 作者 | Y. Zhang ; Z. M. Sun ; Y. C. Zhou |
| 刊名 | Materials Research Innovations
 |
| 出版日期 | 1999 |
| 卷号 | 3期号:2页码:80-84 |
| 关键词 | electronfriction material copper Ti3SiC2 graphite composite self-lubricating ti3sic2 |
| ISSN号 | 1432-8917 |
| 中文摘要 | Cu/Ti3SiC2 composite, a new electrofriction material, was prepared, for the first time, by PM method. The microstructure, mechanical and electrical properties of the Cu/Ti3SiC2 composites were investigated and were compared with those of Cu/graphite composites. The results demonstrated that Cu/Ti3SiC2 composites had superior mechanical properties over Cu/graphite composites. At filer content of less than 20 vol%, the electrical conductivity for Cu/Ti3SiC2 composites was higher than that for Cu/graphite composites; at high filer content, the electrical conductivity for Cu/Ti3SiC2 composites was lower than that for Cu/graphite composites because of the presence of residual pores. It was found that like Cu/graphite composite, Cu/Ti3SiC2 was a self-lubricated material. The compressive yield strength, Brinell hardness, relative ratio of compressive for Cu-30 vol% Ti3SiC2 composites are 307 MPa, 140, 15.7% respectively. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37580]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. Zhang,Z. M. Sun,Y. C. Zhou. Cu/Ti3SiC2 composite: a new electrofriction material[J]. Materials Research Innovations,1999,3(2):80-84. |
| APA | Y. Zhang,Z. M. Sun,&Y. C. Zhou.(1999).Cu/Ti3SiC2 composite: a new electrofriction material.Materials Research Innovations,3(2),80-84. |
| MLA | Y. Zhang,et al."Cu/Ti3SiC2 composite: a new electrofriction material".Materials Research Innovations 3.2(1999):80-84. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。