Preliminary investigation of NiAl-TiB2 composite prepared by reaction milling

文献类型:期刊论文

作者L. Z. Zhou ; J. T. Guo
刊名Journal of Materials Science & Technology
出版日期1999
卷号15期号:5页码:427-430
关键词grain-size ductility microstructure deformation behavior strength tensile 1300-k
ISSN号1005-0302
中文摘要Reaction-milled NiAl-TiB2 composite was fabricated by mechanical alloying elemental powders and hot pressing. TiB2 particles are distributed mostly in grain boundaries of the matrix. The compressive strain to failure of the composite at RT is about twice that of cast NiAl. The compressive yield stress at high temperatures is about 4.5 times higher than that of extruded NiAl, and is also much stronger than XD NiAl-TiB2 composites. Deformation behavior between 1000 similar to 1100 degrees C with different strain rates has been investigated.
原文出处://WOS:000083188600008
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/37616]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
L. Z. Zhou,J. T. Guo. Preliminary investigation of NiAl-TiB2 composite prepared by reaction milling[J]. Journal of Materials Science & Technology,1999,15(5):427-430.
APA L. Z. Zhou,&J. T. Guo.(1999).Preliminary investigation of NiAl-TiB2 composite prepared by reaction milling.Journal of Materials Science & Technology,15(5),427-430.
MLA L. Z. Zhou,et al."Preliminary investigation of NiAl-TiB2 composite prepared by reaction milling".Journal of Materials Science & Technology 15.5(1999):427-430.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。