Pressure dependence of the resistance in polyaniline and poly(o-toluidine) at room temperature
文献类型：期刊论文
| 作者 | Z. X. Bao ; F. Colon ; N. J. Pinto ; C. X. Liu |
| 刊名 | Synthetic Metals
 |
| 出版日期 | 1998 |
| 卷号 | 94期号:2页码:211-213 |
| 关键词 | polyaniline and derivatives pressure dependence resistance electrical-conductivity localization transport transition polymers regime |
| ISSN号 | 0379-6779 |
| 中文摘要 | The electrical resistances of powdered samples of polyaniline and poly(o-toluidine) were measured as a function of pressure using a diamond anvil cell up to 22 GPa at room temperature. Since the primary influence of pressure is sample compression, application of pressure leads to an initial decrease in the resistance (enhanced conductivity) of both samples, indicating greater interchain coherence due to reduced interchain separation. Poly(o-toluidine) is seen to have higher resistance values compared with polyaniline for all pressure values recorded, consistent with the fact that it has greater disorder due to the substitution of the larger methyl group on the polymer backbone. Resistance versus pressure measurements recorded during the loading and unloading cycle show asymmetry, suggesting irreversible structural changes in both samples. The crystallinity in poly(o-toluidine) as deduced from our resistance-pressure data is seen to be slightly less than that for polyaniline. (C) 1998 Elsevier Science S.A. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37627]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. X. Bao,F. Colon,N. J. Pinto,et al. Pressure dependence of the resistance in polyaniline and poly(o-toluidine) at room temperature[J]. Synthetic Metals,1998,94(2):211-213. |
| APA | Z. X. Bao,F. Colon,N. J. Pinto,&C. X. Liu.(1998).Pressure dependence of the resistance in polyaniline and poly(o-toluidine) at room temperature.Synthetic Metals,94(2),211-213. |
| MLA | Z. X. Bao,et al."Pressure dependence of the resistance in polyaniline and poly(o-toluidine) at room temperature".Synthetic Metals 94.2(1998):211-213. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。