Stress-induced phase transformations in a hot-deformed two-phase (alpha(2)+gamma) TiAl alloy
文献类型：期刊论文
| 作者 | J. G. Wang ; L. C. Zhang ; G. L. Chen ; H. Q. Ye |
| 刊名 | Journal of Materials Science
 |
| 出版日期 | 1998 |
| 卷号 | 33期号:10页码:2563-2571 |
| 关键词 | transmission electron-microscopy gamma-titanium aluminides interfacial boundaries intermetallic alloys ti-45al-10nb alloy base alloys deformation |
| ISSN号 | 0022-2461 |
| 中文摘要 | Stress-induced gamma --> alpha(2), alpha(2) --> gamma and gamma --> 9R phase transformations in a hot-deformed Ti-45 at % Al-10 at% Nb alloy have been investigated using high-resolution transmission electron microscopy. The gamma --> alpha(2) phase transformation is an interface-related process. The interfacial superdislocations emitted from the misoriented semicoherent alpha(2)-gamma interface react with each other or with the moving dislocations in the gamma phase, resulting in the formation of the at phase. The nucleation of the alpha(2) --> gamma phase transformation takes place either at the alpha(2)-gamma interfaces or at the stacking faults on the basal plane of alpha(2) phase, and the growth of gamma plate is accomplished by the moving of a/6[1 0 (1) over bar 0] Shockley partials on alternate basal plane (0 0 0 1 )(alpha 2). The 9R structure was usually found to form at incoherent twin or pseudotwin boundaries. During deformation the interfacial Shockley partial dislocations of these incoherent twin and pseudotwin boundaries may glide on (1 1 1), planes into the matrix, resulting in the formation of 9R structure. The interfaces (including alpha(2)-gamma and gamma-gamma interfaces) as well as the crystallographic orientation relationship between the as-received or stress-induced alpha(2), gamma and 9R phase have been analysed. The mechanisms for the stress-induced gamma --> alpha(2), alpha(2) --> gamma and gamma --> 9R phase transformations were also discussed. (C) 1998 Chapman & Hall. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37801]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. G. Wang,L. C. Zhang,G. L. Chen,et al. Stress-induced phase transformations in a hot-deformed two-phase (alpha(2)+gamma) TiAl alloy[J]. Journal of Materials Science,1998,33(10):2563-2571. |
| APA | J. G. Wang,L. C. Zhang,G. L. Chen,&H. Q. Ye.(1998).Stress-induced phase transformations in a hot-deformed two-phase (alpha(2)+gamma) TiAl alloy.Journal of Materials Science,33(10),2563-2571. |
| MLA | J. G. Wang,et al."Stress-induced phase transformations in a hot-deformed two-phase (alpha(2)+gamma) TiAl alloy".Journal of Materials Science 33.10(1998):2563-2571. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。