Temperature dependence of deformation-assisted crystallization in amorphous Fe-78 B13Sig
文献类型：期刊论文
| 作者 | J. Xu ; M. Atzmon |
| 刊名 | Applied Physics Letters
 |
| 出版日期 | 1998 |
| 卷号 | 73期号:13页码:1805-1807 |
| 关键词 | metallic glasses energy alloys transformations fe78b13si9 |
| ISSN号 | 0003-6951 |
| 中文摘要 | Low-energy ball milling of amorphous Fe78B13Si9 has been performed at temperatures between 25 and 250 degrees C. Primary crystallization is observed after milling at elevated temperatures, but not after annealing at the same temperatures. Although milling at room temperature creates nucleation sites for primary crystallization, subsequent annealing at elevated temperature does not result in significant crystallization. Heating by ball impact and contamination by the milling tools during milling are ruled out as the causes for crystallization. The observed behavior is interpreted to be caused by diffusivity enhancement due to milling-produced defects. (C) 1998 American Institute of Physics. [S0003-6951(98)01439-9]. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37837]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Xu,M. Atzmon. Temperature dependence of deformation-assisted crystallization in amorphous Fe-78 B13Sig[J]. Applied Physics Letters,1998,73(13):1805-1807. |
| APA | J. Xu,&M. Atzmon.(1998).Temperature dependence of deformation-assisted crystallization in amorphous Fe-78 B13Sig.Applied Physics Letters,73(13),1805-1807. |
| MLA | J. Xu,et al."Temperature dependence of deformation-assisted crystallization in amorphous Fe-78 B13Sig".Applied Physics Letters 73.13(1998):1805-1807. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。