Consolidation of MA amorphous NiTi powders by spark plasma sintering
文献类型：期刊论文
| 作者 | L. L. Ye ; Z. G. Liu ; K. Raviprasad ; M. X. Quan ; M. Umemoto ; Z. Q. Hu |
| 刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
 |
| 出版日期 | 1998 |
| 卷号 | 241期号:1-2页码:290-293 |
| 关键词 | spark plasma sintering NiTi alloy solid state reaction compaction nickel |
| ISSN号 | 0921-5093 |
| 中文摘要 | Spark plasma sintering, as a recent innovation in rapid powder consolidation was used to sinter amorphous NiTi alloy obtained from mechanical alloying. Densified samples with Ni3Ti, NiTi and NiTi, phases were produced. The grain sizes were retained to within 500 nm at the sintering temperature of 900 degrees C and 1 mu m for the sintering temperature of 1100 degrees C. Based on the results of SEM and TEM, it is found that the formation of crystalline structure is controlled by solid state reaction when the sample was sintered at 900 degrees C, but in the sample compacted at 1100 degrees C, liquid was introduced for the low melting point phase NiTi2 melt. The products after sintering associated with the advantage of spark plasma sintering and the property of amorphous NiTi alloys after mechanical alloying is discussed. (C) 1998 Elsevier Science S.A. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37852]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. L. Ye,Z. G. Liu,K. Raviprasad,et al. Consolidation of MA amorphous NiTi powders by spark plasma sintering[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,1998,241(1-2):290-293. |
| APA | L. L. Ye,Z. G. Liu,K. Raviprasad,M. X. Quan,M. Umemoto,&Z. Q. Hu.(1998).Consolidation of MA amorphous NiTi powders by spark plasma sintering.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,241(1-2),290-293. |
| MLA | L. L. Ye,et al."Consolidation of MA amorphous NiTi powders by spark plasma sintering".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 241.1-2(1998):290-293. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。