Cold-working and heat-cracking in Ni-Cu-base Monel alloy K-500
文献类型：期刊论文
| 作者 | C. Yuan ; H. C. Yang ; Z. X. Wang ; J. T. Guo |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 1998 |
| 卷号 | 8期号:1页码:41195 |
| 关键词 | Monel alloy K-500 cold-working heat cracking mechanical straightening |
| ISSN号 | 1003-6326 |
| 中文摘要 | Cold-working and its effect on heat cracking of Monel alloy K-500 were investigated. The results showed that cold-working hardening is limited for its strong effect on heat cracking, although Monel alloy K-500 has good cold workability. It was revealed that the main reasons of heat cracking, which initiates on the surface of the specimens and propagates intergranularly into the inner during aging, are the residual stress due to cold working, the heat stress due to aging and the surface brittleness occuring in early aging stage. It was proved that mechanical straightening is a beneficial and economical method to prevent Monel alloy K-500 from heat cracking. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37858]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | C. Yuan,H. C. Yang,Z. X. Wang,et al. Cold-working and heat-cracking in Ni-Cu-base Monel alloy K-500[J]. Transactions of Nonferrous Metals Society of China,1998,8(1):41195. |
| APA | C. Yuan,H. C. Yang,Z. X. Wang,&J. T. Guo.(1998).Cold-working and heat-cracking in Ni-Cu-base Monel alloy K-500.Transactions of Nonferrous Metals Society of China,8(1),41195. |
| MLA | C. Yuan,et al."Cold-working and heat-cracking in Ni-Cu-base Monel alloy K-500".Transactions of Nonferrous Metals Society of China 8.1(1998):41195. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。