Effects of grain boundaries on cyclic deformation behavior of copper bicrystals and columnar crystals

文献类型:期刊论文

作者Z. F. Zhang ; Z. G. Wang
刊名Acta Materialia
出版日期1998
卷号46期号:14页码:5063-5072
关键词electron channeling contrast plastic strain amplitudes single-crystals aluminum bicrystals fatigue localization polycrystals metals slip
ISSN号1359-6454
中文摘要In order to reveal the effects of grain boundaries (GBs), the cyclic deformation behavior of a copper columnar crystal containing low-angle GBs, a really grown copper bicrystal RE and a combined bicrystal CB was investigated. The results show that the cyclic stress-strain curve (CSSC) of the copper columnar crystal exhibited a plateau region with saturation resolved shear stress of about 29 MPa over a plastic resolved shear strain range from 6.5 x 10(-4) to 4.7 x 10(-3). The electron channeling contrast technique in scanning electron microscopy (SEM-ECC) was applied to observe the cyclically saturated dislocation structures and persistent slip bands (PSBs). In combining the CSSC with the associated saturation dislocation arrangements, it is seen that the strengthening effect of low-angle GBs is very limited. Meanwhile, the CSSC of the combined bicrystal CB was also found to exhibit a plateau region with the saturation resolved shear stress in the range of 29-30 MPa at the plastic resolved shear strain range From 9 x 10(-4) to 5.58 x 10(-3). However, the bicrystal RE did not display a plateau in its CSSC, and its saturation stress increased with increasing strain amplitude. Surface observations revealed a GB affected zone (GBAZ) with additional slip near the GB in the bicrystal RE. The width W-GB and the volume fraction V-GB of the GBAZ increased with increasing strain amplitude. By comparing the CSSCs of the copper bicrystal CB and RB as well as [(1) over bar 35]//[(1) over bar 35]//[(1) over bar 35]//[(2) over bar 35] and [(2) over bar 35]//[(2) over bar 35] copper bicrystals, the effects of large-angle and low-angle GBs on cyclic deformation behavior were discussed. A GB strengthening model was proposed by introducing a GB resistance Delta tau(as)(B) to PSBs and the mean stress sigma(as)(GB) in the GBAZ. (C) 1998 Acta Metallurgica Inc. Published by Elsevier Science Ltd. All rights reserved.
原文出处://WOS:000076014400022
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/37889]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Z. F. Zhang,Z. G. Wang. Effects of grain boundaries on cyclic deformation behavior of copper bicrystals and columnar crystals[J]. Acta Materialia,1998,46(14):5063-5072.
APA Z. F. Zhang,&Z. G. Wang.(1998).Effects of grain boundaries on cyclic deformation behavior of copper bicrystals and columnar crystals.Acta Materialia,46(14),5063-5072.
MLA Z. F. Zhang,et al."Effects of grain boundaries on cyclic deformation behavior of copper bicrystals and columnar crystals".Acta Materialia 46.14(1998):5063-5072.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。