Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals

文献类型:期刊论文

作者Z. F. Zhang ; Z. G. Wang ; S. X. Li
刊名Fatigue & Fracture of Engineering Materials & Structures
出版日期1998
卷号21期号:11页码:1307-1316
ISSN号8756-758X
关键词fatigue cracking fatigue lives large-angle GBs low-angle GBs PSBs electron channeling contrast low amplitude fatigue stage-i propagation high strain fatigue cyclic deformation single-crystals initiation nucleation metals growth
中文摘要In this paper, the fatigue cracking possibility in different kinds of copper bicrystals with large-angle grain boundaries (GBs) and copper multicrystals containing some low-angle GBs are compared. The results showed that the fatigue cracks, in the copper bicrystals, always nucleated firstly along GBs no matter whether the GBs are perpendicular or parallel to the stress axis. Whereas, for the copper multicrystals containing low-angle GBs, the persistent slip bands (PSBs) are always the preferential sites to initiate fatigue cracks no matter whether low-angle GBs are perpendicular or parallel to the stress axis. Additionally, the fatigue lives of the GBs, and the [(1) over bar 23] and [(3) over bar 35] grains in the [(1) over bar 23] perpendicular to [(3) over bar 35] and [(5) over bar 913] perpendicular to [(5) over bar 79] bicrystals were measured at different cyclic stresses and strain amplitudes. The results show that intergranular fracture always occurred prior to transgranular Fracture in those bicrystals. The fatigue lives increased in the order of the GB, the [(1) over bar 23] and the [(3) over bar 35] grains in the [(1) over bar 23] perpendicular to [(3) over bar 35] bicrystal under cyclic tension-tension loading. On the other hand, the fatigue life of the GB in the [(5) over bar 913] perpendicular to [(5) over bar 79] bicrystal is about two to three times higher than that in the [(1) over bar 23] perpendicular to [(3) over bar 35] bicrystal. Based on these experimental results from the copper bicrystals and multicrystals, it is indicated that the possibility of fatigue cracking increased in the order of low-angle GBs, PSBs and large-angle GBs. It is suggested that both the PSB-GB mechanism and the step mechanism required for GB fatigue cracking were questionable, and the interaction modes of PSBs with GBs may be more important for intergranular fatigue cracking.
原文出处://WOS:000077863300003
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/37891]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Z. F. Zhang,Z. G. Wang,S. X. Li. Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals[J]. Fatigue & Fracture of Engineering Materials & Structures,1998,21(11):1307-1316.
APA Z. F. Zhang,Z. G. Wang,&S. X. Li.(1998).Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals.Fatigue & Fracture of Engineering Materials & Structures,21(11),1307-1316.
MLA Z. F. Zhang,et al."Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals".Fatigue & Fracture of Engineering Materials & Structures 21.11(1998):1307-1316.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。