Microstructure of second-phase particles in Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nd alloy
文献类型：期刊论文
| 作者 | G. P. Li ; D. Li ; Y. Y. Liu ; S. X. Guan ; Q. J. Wang ; D. H. Ping ; Z. Q. Hu |
| 刊名 | Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science
 |
| 出版日期 | 1997 |
| 卷号 | 28期号:8页码:1595-1605 |
| ISSN号 | 1073-5623 |
| 关键词 | strengthened titanium-alloys rapid solidification nanocrystalline materials |
| 中文摘要 | The microstructure of second-phase, particles in the Ti-55 alloy (Ti-5Al;4Sn-2Zr-1 Mo-0.25Si-1Nd) was studied by scanning electron microscopy, transmission electron microscopy (TEM), and high-resolution electron microscopy (HREM) observations. The second-phase particles in the conventional ingot-cast Ti-55 alloy of 1 to 15 mu m in diameter and uniform distribution in matrix were observed, where the majority of these particles are elliptical. The mean free path between the particles is about 46 mu m, and the volume fraction (pct) is 2.35. The second-phase particles typically contain Nd, Sn, and O in substantial amounts, and the content of Nd is the largest in the three elements. The elements Ti, Al, Zr, Mo and Si are depleted in the particles. The second-phase particle consists of either a dark or bright matrix and some small dark blocks dispersed within the matrix. Dark blocks match SnO (orthorhombic, a = 0.500 nm, b = 0.572 nm, and c = 1.120 nm), and the matrix consists of a nanocrystalline phase with a stoichiometric Nd3Sn structure having a space group of Pm3m and lattice parameter of a = 0.344 nm. The grain size of the nanocrystalline Nd3Sn phase is about 3 to 15 nm. The melting range of the second-phase particle is estimated to be 1042 degrees C to 1600 degrees C. The microstructure bf the second-phase particles in the quenched Ti-55 alloy was also studied. Fine and uniform dispersoids (6 to 15 nm in diameter) were observed in the as-quenched state. Some lens-like particles occur at the grain boundaries, other elliptical particles appear within the grains, and some particles within the grains form rows which are parallel to the advancing liquid-solid interface. After annealing at 980 degrees C (1 to 10 hours), of the as-quenched Ti-55 alloy, coarse particles are 17 to 42 nm in average diameter, and the growth of the particles is very slow. The dispersoids in the as-annealed Ti-55 alloy are identified as nanocrystalline Nd5Sn (orthorhombic, Pnmn, a = 0.814 nm, b = 1.732 nm, and c = 0.814 nm) intermetallic compound, and the interface between the Nd5Sn4 phase and the matrix is a typical high-angle grain boundary. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/37993]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. P. Li,D. Li,Y. Y. Liu,et al. Microstructure of second-phase particles in Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nd alloy[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,1997,28(8):1595-1605. |
| APA | G. P. Li.,D. Li.,Y. Y. Liu.,S. X. Guan.,Q. J. Wang.,...&Z. Q. Hu.(1997).Microstructure of second-phase particles in Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nd alloy.Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,28(8),1595-1605. |
| MLA | G. P. Li,et al."Microstructure of second-phase particles in Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nd alloy".Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 28.8(1997):1595-1605. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。