Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film

文献类型:期刊论文

作者X. Peng ; L. J. Zhou ; T. F. Li ; W. T. Wu
刊名Journal of Rare Earths
出版日期1997
卷号15期号:3页码:195-200
关键词rare earths La Ni-La2O3 electrodeposited composite film stainless steel oxidation behavior scales
ISSN号1002-0721
中文摘要The oxidation behaviors of Fe26Cr1Mo with and without the Ni-La2O3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy-dispersive analytical X-ray system (SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 degrees C spalled severely during cooling, while after the stainless steel was coated with the Ni-La2O3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La2O3-modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni-La2O3 composite film.
原文出处://WOS:A1997XY73600008
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/38062]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
X. Peng,L. J. Zhou,T. F. Li,et al. Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film[J]. Journal of Rare Earths,1997,15(3):195-200.
APA X. Peng,L. J. Zhou,T. F. Li,&W. T. Wu.(1997).Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film.Journal of Rare Earths,15(3),195-200.
MLA X. Peng,et al."Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film".Journal of Rare Earths 15.3(1997):195-200.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。