Lattice instability in the solid-state amorphization of Fe(Al) solid solutions by mechanical alloying

文献类型:期刊论文

作者H. W. Sheng ; Y. H. Zhao ; Z. Q. Hu ; K. Lu
刊名Physical Review B
出版日期1997
卷号56期号:5页码:2302-2305
关键词to-glass transition crystal transformation
ISSN号0163-1829
中文摘要Metastable Fe100-xAlx alloys have been formed by ball milling of elemental Fe and Al powders: supersaturated body-centered-cubic solid solutions for x less than or equal to 70, and an amorphous phase for x > 70. Quantitative x-ray-diffraction measurements show that the total root-mean-square displacement (rms) and the static rms in the Fe100-xAlx solid solutions increase significantly with increasing Al content, The total rms at the instability point, however, reaches only 6.8% of the nearest-neighbor distance and is far below the critical value predicted by the Lindemann melting criterion, suggesting that the Lindemann melting criterion is not applicable for the solid-state amorphization. Instead. the Debye temperature of the supersaturated Fe100-xAlx alloys was observed to drop by similar to 22% at the point of amorphization, implying a corresponding softening in the average shear modulus of similar to 40%, which agrees with the microhardness measurements. These results strongly support the empirical elastic instability criterion For the solid-state amorphization process.
原文出处://WOS:A1997XQ61900006
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/38076]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
H. W. Sheng,Y. H. Zhao,Z. Q. Hu,et al. Lattice instability in the solid-state amorphization of Fe(Al) solid solutions by mechanical alloying[J]. Physical Review B,1997,56(5):2302-2305.
APA H. W. Sheng,Y. H. Zhao,Z. Q. Hu,&K. Lu.(1997).Lattice instability in the solid-state amorphization of Fe(Al) solid solutions by mechanical alloying.Physical Review B,56(5),2302-2305.
MLA H. W. Sheng,et al."Lattice instability in the solid-state amorphization of Fe(Al) solid solutions by mechanical alloying".Physical Review B 56.5(1997):2302-2305.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。