Joining of sialon ceramics by Sn-5 at % Ti based ternary active solders
文献类型：期刊论文
| 作者 | A. P. Xian |
| 刊名 | Journal of Materials Science
 |
| 出版日期 | 1997 |
| 卷号 | 32期号:23页码:6387-6393 |
| 关键词 | brazing filler metal silicon-nitride joints interlayer strength aluminum |
| ISSN号 | 0022-2461 |
| 中文摘要 | The effect of a third element, such as silver, copper, indium, nickel or aluminium, on the joining of sialon ceramics with tin-5 at % titanium based ternary active solders was investigated. The content of the third element in the Sn-based solders was varied from 5-40% for Cu, from 5-10% for Ag and Al from 5-20% for In and from 1-5% for Ni. The joining was carried out in vacuum at 1100 K for 20 min. The four point bend testing of a butt joint of a ceramic/ceramic structure with dimensions 40 mm long, 3 mm wide and 4 mm high was used to study the bond strength between the ceramic and the Sn-based solders. The results show that the bond strength of the Sn-based solder with the sialon ceramic varied from 54-103 MPa. Small additions of Cu or Ag (about 5-10%), In (about 5-10%), or Ni (about 1-3%) to the solder is beneficial, but too much Ni (more than 5%) or In (more than 10%) is detrimental. On the other hand, Al in the active solder considerably decreased the bond strength of the solders with the ceramic. Suggestions are made for the selection of the third element in order to improve the bond strength of the soft solders with the ceramic. These include a high surface energy, improving the wetting of the solder on the ceramic and strengthening of the solder. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/38150]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | A. P. Xian. Joining of sialon ceramics by Sn-5 at % Ti based ternary active solders[J]. Journal of Materials Science,1997,32(23):6387-6393. |
| APA | A. P. Xian.(1997).Joining of sialon ceramics by Sn-5 at % Ti based ternary active solders.Journal of Materials Science,32(23),6387-6393. |
| MLA | A. P. Xian."Joining of sialon ceramics by Sn-5 at % Ti based ternary active solders".Journal of Materials Science 32.23(1997):6387-6393. |