Microstructure and mechanical behavior of the NiAl-TiC in situ composite
文献类型：期刊论文
| 作者 | Z. P. Xing ; J. T. Guo ; Y. F. Han ; L. G. Yu |
| 刊名 | Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science
 |
| 出版日期 | 1997 |
| 卷号 | 28期号:4页码:1079-1087 |
| 关键词 | nickel aluminide intermetallics crack deflection processes fracture-toughness compression properties matrix composites interfaces deformation particulate 1200-k 1300-k |
| ISSN号 | 1073-5623 |
| 中文摘要 | The microstructure, interfaces, and mechanical properties of NiAl-matrix composites reinforced by 0 and 20 vol pct TiC particles have been examined. The composites were prepared by the hot-press-aided exothermic synthesis (HPES) technique. Portions of the HPES-processed samples were hot isostatically pressed (''hipped'') at 1165 degrees C/150 MPa for 4 hours or annealed at 1400 degrees C for 48 hours. In the as-fabricated state, TiC particles were generally polygonal and faceted, and the interfaces' between TiC and NiAl were atomically flat, sharp, and generally free from any interfacial phase. At least two orientation relationships between TiC and NiAl were observed. In some cases, thin amorphous layers existed at NiAl/TiC interfaces. After ''hipping,'' the TiC particles tended to become round and the TiC/NiAl interfaces became overlapped. Annealing at 1400 degrees C for 48 hours did not affect the microstructure or the interfacial structure of the composite in most cases. The compressive yield strengths (YSs) from room temperature to 1100 degrees C of the composite were considerably higher than that of the monolithic NiAl. At 980 degrees C, the tensile YS of the composite was approximately 3 times that of the monolithic NiAl. In addition, the ambient fracture toughness of the composite was 50 pct higher than that of the monolithic NiAl. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/38155]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. P. Xing,J. T. Guo,Y. F. Han,et al. Microstructure and mechanical behavior of the NiAl-TiC in situ composite[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,1997,28(4):1079-1087. |
| APA | Z. P. Xing,J. T. Guo,Y. F. Han,&L. G. Yu.(1997).Microstructure and mechanical behavior of the NiAl-TiC in situ composite.Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,28(4),1079-1087. |
| MLA | Z. P. Xing,et al."Microstructure and mechanical behavior of the NiAl-TiC in situ composite".Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 28.4(1997):1079-1087. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。