Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment
文献类型：期刊论文
| 作者 | T. C. Zhang ; X. X. Jiang ; S. Z. Li |
| 刊名 | Corrosion
 |
| 出版日期 | 1997 |
| 卷号 | 53期号:3页码:200-205 |
| 关键词 | corrosive wear embrittlement high-strength low-alloy steel hydrogen-induced damage morphology scanning electron microscopy secondary ion mass spectrometry corrosive wear cracking |
| ISSN号 | 0010-9312 |
| 中文摘要 | Corrosive wear of a high-strength, low-alloy steel (HSLA) was examined in 0.02 mol/L sulfuric acid (H2SO4) solution at different polarized potentials and loads using a pin-on-disc wear device and a potentiostat. Morphologies of the wear tracks were observed by scanning electron microscopy (SEM). Hydrogen content in the surface or subsurface of wear tracks was determined using secondary ion mass spectrometry (SIMS). Results showed the increased material removal with a negative shift of potential in the cathodically polarized range resulted from the synergistic effect of hydrogen-induced damage and mechanical wear from hydrogen evolution on the wear surface. Increases in wear loss with potential in the anodically polarized range resulted from synergism between anodic dissolution and wear. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/38211]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | T. C. Zhang,X. X. Jiang,S. Z. Li. Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment[J]. Corrosion,1997,53(3):200-205. |
| APA | T. C. Zhang,X. X. Jiang,&S. Z. Li.(1997).Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment.Corrosion,53(3),200-205. |
| MLA | T. C. Zhang,et al."Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment".Corrosion 53.3(1997):200-205. |
入库方式： OAI收割
来源：金属研究所