Shear strength at the interface between aluminum and ceramics in model composites fabricated by squeeze casting

文献类型:期刊论文

作者N. Izawa ; Y. X. Lu ; Y. Nishida
刊名Materials Transactions Jim
出版日期1996
卷号37期号:3页码:259-264
关键词squeeze casting metal matrix composite ceramic bonding interface shear strength
ISSN号0916-1821
中文摘要The shear strength at the ceramic-aluminum alloy interface of composites fabricated by squeeze casting was measured. Ceramics used were SiC, Si3N4 and Al2O3, and pure aluminum, JIS AC8A and 2024 alloys were used as matrices. The shear strength was measured by pushing out a rectangular bar-like ceramic (cross-section: 5 mm x 10 mm) which were enveloped in an aluminum alloy by squeeze casting. The good bonding between ceramics and aluminum alloys was obtained by squeeze casting. Fracture of pure aluminum matrix composites occurred in the aluminum site near the interface. However, fracture occurred at the interface in the case of SiC-AC8A alloy composite and the shear strength is slightly lower than that of the pure aluminum. Fracture behavior of AC8A matrix composites is classified into three stages; initial linear stage, debonding and sliding. The shear strength was measured up to 573 K for each alloy, and decreased linearly with increasing temperature. The shear strength is much related to the roughness of the ceramic surface and increases with the increase in the roughness. The influence of heat treatment on the shear strength was also examined. The shear strength of SiC-pure aluminum did not change by heating for 16 h at 823 K, but that of SiC-2024 decreased.
原文出处://WOS:A1996UJ70000011
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/38305]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
N. Izawa,Y. X. Lu,Y. Nishida. Shear strength at the interface between aluminum and ceramics in model composites fabricated by squeeze casting[J]. Materials Transactions Jim,1996,37(3):259-264.
APA N. Izawa,Y. X. Lu,&Y. Nishida.(1996).Shear strength at the interface between aluminum and ceramics in model composites fabricated by squeeze casting.Materials Transactions Jim,37(3),259-264.
MLA N. Izawa,et al."Shear strength at the interface between aluminum and ceramics in model composites fabricated by squeeze casting".Materials Transactions Jim 37.3(1996):259-264.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。