SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS OF TIC AND NBC BY MECHANICAL ALLOYING
文献类型：期刊论文
| 作者 | Z. G. Liu ; L. L. Ye ; J. T. Guo ; G. S. Li ; Z. Q. Hu |
| 刊名 | Journal of Materials Research
 |
| 出版日期 | 1995 |
| 卷号 | 10期号:12页码:3129-3135 |
| 关键词 | elemental powders carbides mosi2 |
| ISSN号 | 0884-2914 |
| 中文摘要 | Titanium and niobium carbides have been synthesized through self-propagating high-temperature reaction by mechanically alloying the elemental powder mixtures. It is found that this reaction is very similar to the conventional self-propagating high-temperature synthesis (SHS) process, but the ignition of the reaction is identified to be the mechanical collisions instead of heating the materials. Analysis of the products reveals that the final products of the Ti-C system are in good agreement with the equilibrium phase diagram, showing less relation with the alloying process. The decrease of the C content shortens the milling time prior to the SHS reaction of TiC by promoting the intimate mixing of the components, but lowers the heat release of the reaction and makes the propagation of the reaction more slowly. The SHS reaction during the mechanical alloying of the Nb-C system shows little difference, but the decrease of the C content can hardly influence the milling time prior to the reaction. By lowering the heat release of the SHS reaction of NbC, it lowers the reaction propagating rate. Mechanical alloying Nb50C50 and Nb55C45 results in the formation of NbC, while mechanical alloying Nb60C40 results in NbC + Nb instead of NbC + Nb2C according to the phase diagram. It was attributed to the fact that the rapid SHS reaction favors the formation of NbC, but hinders the occurrence of Nb2C phase through slow diffusion between NbC and the residual Nb. The measurement of the lattice parameters of TiC and NbC for different composition affirms the observed results. The particle sizes of obtained TiC and NbC are very fine at around or even less than I mu m. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/38622]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. G. Liu,L. L. Ye,J. T. Guo,et al. SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS OF TIC AND NBC BY MECHANICAL ALLOYING[J]. Journal of Materials Research,1995,10(12):3129-3135. |
| APA | Z. G. Liu,L. L. Ye,J. T. Guo,G. S. Li,&Z. Q. Hu.(1995).SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS OF TIC AND NBC BY MECHANICAL ALLOYING.Journal of Materials Research,10(12),3129-3135. |
| MLA | Z. G. Liu,et al."SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS OF TIC AND NBC BY MECHANICAL ALLOYING".Journal of Materials Research 10.12(1995):3129-3135. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。