EFFECTS OF B+ AND CR+ ION-IMPLANTATION ON THE OXIDATION OF NI3AL
文献类型:期刊论文
作者 | C. Mei ; S. Patu ; S. Changxu ; S. Jianian |
刊名 | Journal of Materials Science
![]() |
出版日期 | 1993 |
卷号 | 28期号:20页码:5508-5513 |
ISSN号 | 0022-2461 |
中文摘要 | Ni3Al samples were implanted with different doses of 150 keV B+ and Cr+ ions to modify the surface region and the high-temperature oxidation behaviour was tested. The surface layer structure was investigated by Auger electron spectroscopy, and transmission electron microscopy, secondary ion mass spectroscopy and optical microscopy before and after testing. The experimental results show that boron atoms exist in the form of interstitial atoms. No evidence was found that any new phase existed in boron implanted Ni3Al. Implanted Ni3Al alloy has better oxidation resistance than the unimplanted ones at 900-degrees-C. For B+-implanted Ni3Al, the oxide layer is basically composed of fine-grained NiO inner layer and an a-Al2O3 outer layer. Boron is oxidized into B2O3 of comparatively larger grain size. B2O3 particles are enriched at grain boundaries and defects. This curtails the short-circuit transportation of oxygen and improves the oxidation resistance of Ni3Al. Implantation with Cr+ and B+ combines the good effects of both elements and produces a remarkable improvement on the oxidation resistance. The effects of implanted elements and the possible reaction mechanisms are discussed. |
原文出处 | |
公开日期 | 2012-04-14 |
源URL | [http://ir.imr.ac.cn/handle/321006/39098] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | C. Mei,S. Patu,S. Changxu,et al. EFFECTS OF B+ AND CR+ ION-IMPLANTATION ON THE OXIDATION OF NI3AL[J]. Journal of Materials Science,1993,28(20):5508-5513. |
APA | C. Mei,S. Patu,S. Changxu,&S. Jianian.(1993).EFFECTS OF B+ AND CR+ ION-IMPLANTATION ON THE OXIDATION OF NI3AL.Journal of Materials Science,28(20),5508-5513. |
MLA | C. Mei,et al."EFFECTS OF B+ AND CR+ ION-IMPLANTATION ON THE OXIDATION OF NI3AL".Journal of Materials Science 28.20(1993):5508-5513. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。