FATIGUE PROPERTIES OF HYDRIDED TITANIUM CONDENSER TUBES
文献类型：期刊论文
| 作者 | W. H. Hartt ; L. Liu |
| 刊名 | Corrosion
 |
| 出版日期 | 1992 |
| 卷号 | 48期号:2页码:172-176 |
| 关键词 | hydrided titanium condenser tubes fatigue seawater cathodic protection remaining life |
| ISSN号 | 0010-9312 |
| 中文摘要 | Fatigue experiments have been performed on hydrided condenser tubes removed from a coastal power plant. Experimental phase of the study developed S-N data for hydride penetration depths ranging from 0 to 50 percent of wall thickness. This revealed about a 75 percent reduction in endurance limit with progressive hydriding over this penetration range. From the relationship between endurance limit and degree of hydriding, it was projected that a fracture mechanics evaluation could be applied where the hydride penetration depth was equivalent to a crack. It was concluded that residual fatigue strength of tubes hydrided to 50 percent of the wall thickness was approximately five times greater than the cyclic service stress plus a factor of safety. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/39224]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. H. Hartt,L. Liu. FATIGUE PROPERTIES OF HYDRIDED TITANIUM CONDENSER TUBES[J]. Corrosion,1992,48(2):172-176. |
| APA | W. H. Hartt,&L. Liu.(1992).FATIGUE PROPERTIES OF HYDRIDED TITANIUM CONDENSER TUBES.Corrosion,48(2),172-176. |
| MLA | W. H. Hartt,et al."FATIGUE PROPERTIES OF HYDRIDED TITANIUM CONDENSER TUBES".Corrosion 48.2(1992):172-176. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。