Cold Crystallization Behavior of Polyamide 6 in PS-g-PA6 Graft Copolymers
文献类型：期刊论文
| 作者 | Shi D ; Wang XY ; Shi HC ; Yin JH ; Li RKY ; Hu GH |
| 刊名 | journal of polymer science part b-polymer physics
 |
| 出版日期 | 2010 |
| 卷号 | 48期号:1页码:65-73 |
| 关键词 | IMMISCIBLE POLYMER BLENDS SIZED PA6 DROPLETS DIFFERENTIAL SCANNING CALORIMETRY ASYMMETRIC DIBLOCK COPOLYMERS CONFINED CRYSTALLIZATION BLOCK-COPOLYMERS FRACTIONATED CRYSTALLIZATION ISOTHERMAL CRYSTALLIZATION DISPERSED MICROMETER ISOTACTIC POLYPROPYLENE |
| ISSN号 | 0887-6266 |
| 通讯作者 | li rky |
| 中文摘要 | tem micrographs show that the pa grafts of ps-g-pa6 graft copolymers, which are obtained directly by extracting homo-pa6 out from the homo-pa6/ps-g-pa6 blends, are in the form of wormlike structure. the wormlike pa6 domains can shrink into droplets after annealing at 250 degrees c for 15 min. the diameter of the droplet determined by tem and saxs is in the range of 50-60 nm. this article reports on a unique crystallization behavior of the pa6 grafts in ps-g-pa6 graft copolymers. in a dsc cooling scan, pa6 grafts do not crystallize from the melt with a cooling rate of 10 degrees c/min. however, there is a cold crystallization peak around 65 degrees c in the subsequent heating scan. this cold crystallization phenomenon, which has not yet been reported in the literature till now, follows well the homogeneous nucleation mechanism and is depressed at relatively slow cooling rates (2 degrees c/min) or even completely eliminated after annealing within a specific temperature range. it may be caused by the slow diffusion or transport rate of the less flexible pa6 grafts to the crystal fronts when crystallization takes place around its glass transition temperature. (c) 2009 wiley periodicals, inc. j polym sci part 8: polym phys 48: 65-73, 2010 |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000273251700007 |
| 公开日期 | 2012-06-07 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/43992]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Shi D,Wang XY,Shi HC,et al. Cold Crystallization Behavior of Polyamide 6 in PS-g-PA6 Graft Copolymers[J]. journal of polymer science part b-polymer physics,2010,48(1):65-73. |
| APA | Shi D,Wang XY,Shi HC,Yin JH,Li RKY,&Hu GH.(2010).Cold Crystallization Behavior of Polyamide 6 in PS-g-PA6 Graft Copolymers.journal of polymer science part b-polymer physics,48(1),65-73. |
| MLA | Shi D,et al."Cold Crystallization Behavior of Polyamide 6 in PS-g-PA6 Graft Copolymers".journal of polymer science part b-polymer physics 48.1(2010):65-73. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。