Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl(11)O(19) composite coatings in molten sulfate-vanadate salt
文献类型：期刊论文
| 作者 | Chen XL ; Zhao Y ; Gu LJ ; Zou BL ; Wang Y ; Cao XQ |
| 刊名 | corrosion science
 |
| 出版日期 | 2011 |
| 卷号 | 53期号:6页码:2335-2343 |
| 关键词 | THERMAL BARRIER COATINGS LANTHANUM HEXAALUMINATE NEXT-GENERATION SODIUM-SULFATE ZIRCONIA YTTRIA HEXALUMINATE DEGRADATION OXIDE RESISTANCE |
| ISSN号 | 0010-938x |
| 通讯作者 | cao xq |
| 中文摘要 | hot corrosion studies of thermal barrier coatings (tbcs) with different ysz/lamgal(11)o(19) (lama) composite coating top coats were conducted in 50 wt.% na(2)so(4) + 50 wt.% v(2)o(5) molten salt at 950 degrees c for 60 h. results indicate that tbcs with composite coating top coats exhibit superior oxidation and hot corrosion resistances to the tbc with the traditional ysz top coat, especially for which has a lama overlay. the presence of lama can effectively restrain the destabilization of ysz at the expense of its own partial degradation. the hot corrosion mechanism of lama coating and the composite coatings have been explored. (c) 2011 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44606]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Chen XL,Zhao Y,Gu LJ,et al. Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl(11)O(19) composite coatings in molten sulfate-vanadate salt[J]. corrosion science,2011,53(6):2335-2343. |
| APA | Chen XL,Zhao Y,Gu LJ,Zou BL,Wang Y,&Cao XQ.(2011).Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl(11)O(19) composite coatings in molten sulfate-vanadate salt.corrosion science,53(6),2335-2343. |
| MLA | Chen XL,et al."Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl(11)O(19) composite coatings in molten sulfate-vanadate salt".corrosion science 53.6(2011):2335-2343. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。