Effects of samarium on microstructures and tensile properties of Mg-5Al-0.3Mn alloy
文献类型：期刊论文
| 作者 | Wang JL ; Wang LD ; Wu YM ; Wang LM |
| 刊名 | materials science and engineering a-structural materials properties microstructure and processing
 |
| 出版日期 | 2011 |
| 卷号 | 528期号:12页码:4115-4119 |
| 关键词 | AZ91 MAGNESIUM ALLOY CAST MG-ALLOYS MECHANICAL-PROPERTIES ELEVATED-TEMPERATURE BASE ALLOY CREEP SR ADDITIONS PHASES |
| ISSN号 | 0921-5093 |
| 通讯作者 | wang lm |
| 中文摘要 | microstructures and tensile properties of mg-5al-0.3mn-xsm (x = 0, 1, 2 and 3 wt.%) alloys prepared by metal mould casting method were investigated. it was demonstrated that mg-5al-0.3mn alloy was mainly composed of alpha-mg and beta-mg(17)al(12) phases. however, the other two precipitates (al(11)sm(3) and al(2)sm) were observed along grain boundaries in the alloys containing sm. the amount of al(11)sm(3) and al(2)sm precipitates was increased with the increment of sm content. meanwhile, volume fraction of beta-mg(17)al(12) phase was decreased. moreover, the morphology of (beta-mg(17)al(12) was altered from bulk bone-like shape to spherical one. tensile results showed that mg-5al-0.3mn-2sm alloy exhibited the highest tensile properties both at room temperature and 150 degrees c. compared with ultimate tensile strength (uts), yield strength (ys) and elongation (epsilon) of mg-5al-0.3mn alloy, uts, ys and e of mg-5al-0.3mn-2sm alloy were enhanced by 30%, 45% and 35% at room temperature, and by 17,%, 48% and 96% at 150 degrees c, respectively. the improvement of tensile properties was attributed to the decreased amount of beta-mg(17)al(12) and its refined morphology, and high thermal stable al(11)sm(3) and al(2)sm precipitates which effectively prohibited dislocation movement and grain boundary sliding during deformation process. (c) 2011 elsevier b.v. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000289389400024 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44635]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang JL,Wang LD,Wu YM,et al. Effects of samarium on microstructures and tensile properties of Mg-5Al-0.3Mn alloy[J]. materials science and engineering a-structural materials properties microstructure and processing,2011,528(12):4115-4119. |
| APA | Wang JL,Wang LD,Wu YM,&Wang LM.(2011).Effects of samarium on microstructures and tensile properties of Mg-5Al-0.3Mn alloy.materials science and engineering a-structural materials properties microstructure and processing,528(12),4115-4119. |
| MLA | Wang JL,et al."Effects of samarium on microstructures and tensile properties of Mg-5Al-0.3Mn alloy".materials science and engineering a-structural materials properties microstructure and processing 528.12(2011):4115-4119. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。