Drawing-induced Crystallization Behavior and Brill Transition of Nylon 1010
文献类型：期刊论文
| 作者 | Wang JK ; Zhao GS ; Zhou YC |
| 刊名 | chemical journal of chinese universities-chinese
 |
| 出版日期 | 2011 |
| 卷号 | 32期号:5页码:1225-1230 |
| 关键词 | FOLDED LAMELLAR CRYSTALS TEMPERATURE DEPENDENCE |
| ISSN号 | 0251-0790 |
| 通讯作者 | wang jk |
| 中文摘要 | the crystal transitions and crystal orientations of nylon 1010 drawing-induced at different drawing temperatures(t(d)) and drawing ratios(lambda) were studied by differential scanning calorimetry(dsc), wide-angle x-ray diffraction(waxd) and two dimensional (2d) waxd experiments. the results show that drawing is favorable to the transition of delta' form from a form of nylon 1010 and so-called brill transition became more obviously with drawing ratio increasing under the same temperature. new relationship of crystal form versus temperature was first discovered in which delta' form of nylon 1010 could be gradually transformed into a form when drawn at higher drawing temperature. this is distincted from the crystallization performance of nylon 1010 under thermal effect without drawing. the measurements of orientation degrees, based on 2d waxs experiments, showed that crystal orientations were solely decided by the drawing ratios. furthermore, the d spacing of (002) reflections increased with the drawing ratios, which also showed the dependence of long axis increasment on the drawing orientation. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 中文 |
| WOS记录号 | WOS:000291175800042 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44642]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang JK,Zhao GS,Zhou YC. Drawing-induced Crystallization Behavior and Brill Transition of Nylon 1010[J]. chemical journal of chinese universities-chinese,2011,32(5):1225-1230. |
| APA | Wang JK,Zhao GS,&Zhou YC.(2011).Drawing-induced Crystallization Behavior and Brill Transition of Nylon 1010.chemical journal of chinese universities-chinese,32(5),1225-1230. |
| MLA | Wang JK,et al."Drawing-induced Crystallization Behavior and Brill Transition of Nylon 1010".chemical journal of chinese universities-chinese 32.5(2011):1225-1230. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。